Abstract:A series of high molar mass terpolymers is synthesized by ring-opening polymerization of L-lactide (LLA), 1, 3-trimethylene carbonate (TMC) and glycolide (GA). A totally bioresorbable composite is obtained by reinforcing a terpolymer matrix with plasma treated poly (L-lactide-co-glycolide) (PLGA) short fibers. Solution cast films of the various materials are allowed to degrade at 37 C at pH 8.5 Tris buffer using proteinase K, in comparison with a PLLA-TMC copolymer and a PLLA homopolymer. Degradation is monitored by using various analytical techniques such as gravimetry, DSC, GPC, H-1 NMR and SEM. The results show that the enzymatic degradation rate of PLLA-TMC-GA terpolymers with predominant LLA component is affected by both the average LLA block length (I-LLA) and crystallinity. A shorter average LLA block length results in lower crystallinity, which will lead to faster degradation. However, too short average LLA block length (i.e. I-LIA <= 4.0) can retard the degradation process. The composition of the copolymers remains unchanged during degradation. In contrast, the molar mass decreases due to hydrolytic chain cleavage in the bulk. Similarly, thermal property changes are observed with increase of the melting temperature and melting enthalpy in most cases. SEM observation strongly supports a surface erosion mechanism. The composite PLTG95/5/5C exhibits lower mass loss rate as compared to neat PLTG95/5/5 due to the presence of PLGA fibers which are non-degradable by proteinase K. On the other hand, the composite shows much faster molar mass loss rate than PLTG95/5/5 because the rapid hydrolytic degradation of PLGA fibers speeds up the degradation of the matrix by internal autocatalysis. (C) 2014 Elsevier Ltd. All rights reserved.

[Preparation and In-Vitro Degradation of Polylactide and Poly(l-Lactide-co-glycolide)].

Preparation and Properties of Polyglycolide , Poly(L-lactide) and Poly(L-lactide-co-glycolide)

In Vitro Degradation Behavior of L-Lactide/Trimethylene Carbonate/Glycolide Terpolymers and A Composite with Poly(L-Lactide-Co-Glycolide) Fibers

Synthesis of polylactides and copolymers for surface coating of cardiovascular stent

Synthesis and Characterization of Poly(L-lactide-co-glycolide)

In vitro hydrolytic degradation properties of poly(D, L-lactic acid) / poly(L-lactide-co-ε-caprolactone) blend films

Preparation and properties of a biodegradable polymer as a novel drug delivery system

In vitro and in vivo degradation of poly(L: -lactide-co-glycolide) films and scaffolds

Preparation, mechanical, and thermal properties of biodegradable polyesters/poly(lactic acid) blends

Study on the Biocompatibility and Degradation Behavior of Polyl(l-lactide-co-glycolide) in Vitro and in Vivo

Modification and application of polylactide

Enzyme-catalyzed Degradation Behavior of L-Lactide/trimethylene Carbonate/glycolide Terpolymers and Their Composites with Poly(l-Lactide-co-glycolide) Fibers

SYNTHESIS AND CHARACTERIZATION OF COPOLYMER LACTIDE AND ETHYLENE CARBONATE

Synthesis, Characterization and Application of Poly(lactic-co-glycolic acid) with a Mass Ratio of Lactic to Glycolic Segments of 52/48

Preparation of PLGA and PLGA-PEG-PLGA Hydrogels

Degradation Behaviors of Polylactic Acid, Polyglycolic Acid, and Their Copolymer Films in Simulated Marine Environments

Synthesis and Characterization of a Novel Biodegradable Polymer Poly(lactic Acid–glycolic Acid‐4‐hydroxyproline)

In Vivo Degradation of Copolymers Prepared from L-Lactide, 1,3-Trimethylene Carbonate and Glycolide As Coronary Stent Materials

Structure, Properties, and in Vitro Degradation Behavior of Biodegradable Poly(l‐lactic Acid)‐trimethylene Carbonate‐glycolide Terpolymer

Preparation of Poly(lactide-Co-glycolide-co-caprolactone) Nanoparticles and Their Degradation Behaviour in Aqueous Solution

Effect of poly(lactic-co-glycolic acid) blend ratios on the hydrolytic degradation of poly(para-dioxanone)