Abstract:CuO-based catalysts are usually used for CO oxidation owing to their low cost and excellent catalytic activities. In this study, a series of metal oxide (La2O3, Fe2O3, PrO2, Sm2O3, and MnO2)-doped CuO-based catalysts with mesoporous Ce0.8Zr0.2O2 support were simply prepared by the incipient impregnation method and used directly as catalysts for CO catalytic oxidation. These mesoporous catalysts were systematically characterized by X-ray powder diffraction (XRD), N2 physisorption, transmission electron microscopy (TEM), energy-dispersed spectroscopy (EDS) mapping, X-ray photoelectron spectroscopy (XPS), and H2 temperature programmed reduction (H2-TPR). It was found that the CuO and the dopants were highly dispersed among the mesoporous framework via the incipient impregnation method, and the strong metal framework interaction had been formed. The effects of the types of the dopants and the loading amounts of the dopants on the low-temperature catalytic performances were carefully studied. It was concluded that doped transition metal oxides could regulate the oxygen mobility and reduction ability of catalysts, further improving the catalytic activity. It was also found that the high dispersion of rare earth metal oxides (PrO2, Sm2O3) was able to prevent the thermal sintering and aggregation of CuO-based catalysts during the process of calcination. In addition, their presence also evidently improved the reducibility and significantly reduced the particle size of the CuO active sites for CO oxidation. The results demonstrated that the 15CuO-3Fe2O3/M-Ce80Zr20 catalyst with 3 wt. % of Fe2O3 showed the best low-temperature catalytic activity toward CO oxidation. Overall, the present Fe2O3-doped CuO-based catalysts with mesoporous nanocrystalline Ce0.8Zr0.2O2 solid solution as support were considered a promising series of catalysts for low-temperature CO oxidation.

Low Temperature CO Oxidation on Ni-promoted CuO-CeO2 Catalysts

Atomically Incorporating Ni into Mesoporous CeO2 Matrix via Synchronous Spray-Pyrolysis as Efficient Noble-Metal-Free Catalyst for Low-Temperature CO Oxidation

Promotional role of ceria on cobaltosic oxide catalyst for low-temperature CO oxidation

Low Temperature Oxidation of CO over CuO-CeO_2 Catalyst Prepared by Solid-State Chemical Reaction

CeO2 nanoparticles modified by CuO nanoparticles for low-temperature CO oxidation with high catalytic activity

Facile Design of Highly Effective CuCexCo1–xOy Catalysts with Diverse Surface/Interface Structures Toward NO Reduction by CO at Low Temperatures

CO Oxidation over Metal Oxide (La2O3, Fe2O3, PrO2, Sm2O3, and MnO2) Doped CuO-Based Catalysts Supported on Mesoporous Ce0.8Zr0.2O2 with Intensified Low-Temperature Activity

Low temperature oxidation of CO over CuO-Ce02 catalyst prepared by solid-stale chemical reaction

Promotional Effect of Indium on the CuO-CeO2 Catalysts for Low-Temperature CO Oxidation

Comparative study of CuO/Ce0.7Sn0.3O2, CuO/CeO2 and CuO/SnO2 catalysts for low-temperature CO oxidation

An Excellent Support of Pd–Fe–Ox Catalyst for Low Temperature CO Oxidation: CeO2 with Rich (200) Facets

Comparative Study on Catalytic Performances for Low-temperature CO Oxidation of Cu–Ce–O and Cu–Co–Ce–O Catalysts

Low-temperature CO Oxidation over CuO-CeO2/SiO2 Catalysts: Effect of CeO2 Content and Carrier Porosity

Mesoporous NiO–CeO2 Catalysts for CO Oxidation: Nickel Content Effect and Mechanism Aspect

Effect of Fe Doping on the Catalytic Performance of CuO–CeO2 for Low Temperature CO Oxidation

CeO2 nanorods supported CuOx-RuOx bimetallic catalysts for low temperature CO oxidation

Synthesis, characterization of CuO/Ce0.8Sn0.2O2 catalysts for low-temperature CO oxidation

Activities of supported copper oxide catalysts in the NO+CO reaction at low temperatures

Transition Metal (fe2o3, Co3O4 and NiO)-Promoted CuO-Based Α-Mno2 Nanowire Catalysts for Low-Temperature CO Oxidation

Nickel foam supported CuCe mixed metal oxide as monolith catalyst for NO removal

CeO2 nanorods supported M-Co bimetallic oxides (M = Fe, Ni, Cu) for catalytic CO and C3H8 oxidation