Martensitic transformation and magnetic properties of Heusler alloy Ni–Fe–Ga ribbon
Z.H. Liu,H. Liu,X.X. Zhang,M. Zhang,X.F. Dai,H.N. Hu,J.L. Chen,G.H. Wu
DOI: https://doi.org/10.1016/j.physleta.2004.06.088
IF: 2.707
2004-01-01
Physics Letters A
Abstract:The martensitic transformation and magnetic properties of ferromagnetic shape memory alloy Ni50+xFe25−xGa25 (x=−1, 0, 1, 2, 3, 4) ribbons have been systematically studied. It has been found that with the increase of Ni concentration, the martensitic transformation temperature increases, but the Curie temperature decreases. Both the two-step thermally induced structural transformation and the one-step transition have been observed in NiFeGa alloys with different compositions. It is found that the two-step transition became the one-step transition after the ribbon being heat treated at 873 K or higher. X-ray diffraction patterns show that only L21→B2 transition occurs in the samples treated at 873 K, while the γ phase will form in the samples treated at higher temperature. Transmission electron microscopy (TEM) studies show that the alloys with martensitic transformation temperature above the room temperature are non-modulated martensite with the large domain size, being different from the stoichiometric Ni2FeGa alloy that is a modulated martensite with small domain size. The influences of Fe substitution for Ni in Ni2FeGa on the saturation magnetization and exchange interaction are also discussed.