Abstract:Aluminium Matrix Composites reinforced with ceramic particles (e.g. SiC, Al2O3, graphite and fly ash) are actually advanced engineering materials. These materials can be characterised by superior mechanical and thermal properties. However, the addition of the reinforcement particles could significantly changing corrosion behaviour of aluminium matrix composites. The corrosion resistance of aluminium matrix composites is determined by several factors such as: variety of aluminium alloy matrix and reinforcement type combinations, manufacturing technology, microstructure of composite and interfacial reactions reinforcement/matrix. This paper presents microstructural characteristic and susceptibility to pitting corrosion of on aluminium-based metal matrix (Al-Si) composites reinforced with graphite (5.7 wt. %), SiC (20 vol. %) and fly ash (9.0 wt. %) particles. The corrosion resistance experiments were carried out by accelerated electrochemical studies using the potentiodynamic method (in the 3.5 wt. % NaCl aqueous solution, pH 7.0, at 25oC). The corrosion behaviour of composite with fly ash particles was studied further by immersion tests for 50 days (3.5 wt. % NaCl). The polarisation curves, corrosion potentials (corrosion Ecorr, pitting Epit and repassivation Erp) and surface morphology after corrosion tests were estimated. It was found that: (1) the electrochemical data and microstructure observations after corrosion tests confirms that incorporation of reinforcement particles (graphite, SiC, fly ash) into aluminium matrix causes the increase of susceptibility to pitting corrosion of the composites in comparison with unreinforced matrix alloys, (2) the enhanced pitting corrosion of Al/fly ash, Al/SiC and Al/GR composites is associated with the pores, multiphasic character of composites (e.g. the releases of intermetallic Al3Ni phase), reactions at the interface reinforcement/matrix and formation of galvanic couples favourable to corrosion. The same factors also determine the properties of oxide film forming on the materials surface.

Corrosion Behavior of SiCp/7A04 Aluminum Matrix Composites

Effect of Heat Treatment on Microstructure and Corrosion Resistance of SiCp/Al 2124 Composite

Corrosion Behavior of SiC_w?Al Compoite

Aging Behavior and Precipitation Kinetics of SiCp/6061AI Composites

Effect of Sic Particulates on the Corrosion Behavior of Extruded Az91/Sicp Composites During the Early Stage of Exposure

Particle agglomeration and mechanical properties of SiCp/Al-Si composites

THE INFLUENCE OF CERAMIC PARTICLES ON THE CORROSION PROPERTIES OF NOVEL TI750 MATRIX ALLOY

Investigation of the Corroded Surface of SiCw/Al Composite

Corrosion studies on aluminium-based metal matrix composites reinforced with graphite, SiC and fly ash particles

Revealing the Influence of SiC Particle Size on the Hot Workability of SiCp/6013 Aluminum Matrix Composites

Anodizing Protection for SiCp/2024Al Composite Material

Corrosion behavior of Al4SiC4/SiC ceramics exposed to molten calcium‐magnesium‐alumino‐silicate at 1350°C in air

Microstructure and Thermal Conduction Property of SiCp/Al- Si Composite with High Reinforcement Content

Studies on the corrosion resistance of Al7075 / SiC metal matrix composites in an alkaline environment

Revealing corrosion behavior of B4C/pure Al composite at different interfaces between B4C particles and Al matrix in NaCl electrolyte

Aging Behavior of High Volume Fraction SiC Particles Reinforced 2024al Composite

Microstructure and Corrosion Resistance of SiC Nanoparticles Reinforced Ceramic Composite Coating on Mg-Li Based Composite by Micro-Arc Oxidation

Fundamental Study of SiCp/Al Composites in Electronic Packaging Applications

Electrochemical Corrosion Behavior of Al–Si Alloy Composites Reinforced with in Situ TiB2 Particulate

Effect of SiC doping on corrosion behavior of Cf/Mg composites

Preparation, microstructure, stability in magnesium metallurgy environment of SiC composites