Porous Olive-Like BiVO4: Alcoho-hydrothermal Preparation and Excellent Visible-Light-driven Photocatalytic Performance for the Degradation of Phenol

Haiyan Jiang,Hongxing Dai,Xue Meng,Kemeng Ji,Lei Zhang,Jiguang Deng
DOI: https://doi.org/10.1016/j.apcatb.2011.04.026
2011-01-01
Abstract:Bismuth vanadates with multiple morphologies and/or porous structures were prepared using the alcoho-hydrothermal strategy with bismuth nitrate and ammonium metavanadate as metal source, NaOH as pH adjustor, ethanol and ethylene glycol as solvent, and/or dodecylamine (DA), oleylamine (OL) or oleic acid (OA) as surfactant. The materials were characterized by means of the XRD, Raman, TGA/DSC, FT-IR, BET, SEM, TEM, XPS, and UV–vis techniques. The photocatalytic performance of the as-obtained samples was evaluated for the degradation of phenol in the presence of a small amount of H2O2 under visible-light irradiation, and the effect of phenol concentration on the photocatalytic activity was also examined. It is found that the surfactant and pH value had a significant influence on the particle morphology and even the crystalline structure of the product. Porous olive-like monoclinic BiVO4 samples could be prepared with DA, OL or OA as surfactant at pH=1.5 or 3.0 and alcoho-hydrothermal temperature=100°C. With DA as surfactant at an alcoho-hydrothermal temperature of 100°C, short-rod-like monoclinic BiVO4 and porous sheet-layered spherical orthorhombic Bi4V2O11 were obtained when the pH value of the precursor solution was raised to 7.0 and 11.0, respectively. Among the BiVO4 samples, the porous olive-like one with a surface area of 12.7m2/g exhibited the best visible-light-driven photocatalytic performance for phenol degradation. It is concluded that the excellent photocatalytic activity of the porous olive-like BiVO4 sample was associated with its higher surface area and surface oxygen vacancy density, porous structure, lower bandgap energy, and unique morphology.
What problem does this paper attempt to address?