Abstract:TiO_2-SiO_2 composite powders stabilized at high temperature with high photocatalytic activity were prepared using a two-step hydrothermal method,with tetrabutyl titanate and tetraethyl orthosilicate as the materials. The powders were then characterized by means of dynamic light-scattering size analysis,DSC,FT-IR,TEM and XRD.The results of particle size analysis indicate that the composite powders disperse well in a size range of 10～30 nm with narrow distribution.DSC results show that the addition of silica greatly improves the high-temperature stability of titania dioxide.Phase analysis results demonstrate that the high-temperature stability of anatase titania becomes better with the increase of SiO_2 content,and that the composite powders with a TiO_2/SiO_2 molar ratio of 1:l maintain as anatase phase after being treated at 1200℃for 2h.FT-IR spectra show that there is no Ti—O—Si bonds in the.TiO_2-SiO_2 composite powders before and after the treatment at 800℃for 2h.Moreover,according to the degradation of aqueous methyl orange by TiO_2-SiO_2 composite powders under UV irradiation,it is found that (1) the photocatalysis of the composite powders without heat treatment is similar to that of commercial P25 TiO_2 powders;(2) the photocatalytic activity of the composite powders after the heat treatment at 800 and 1 000℃for 2 h is much higher than that of P25;and(3) after the heat treatment at 1200℃for 2 h,the photocatalytic activity of the composite powders becomes poorer.

Preparation of TiO_2-SiO_2 Composite Powders Stabilized at High Temperature by Two-Step Hydrothermal Method