Abstract:We report a synthesis method for highly monodisperse Cu-Pt alloy nanoparticles. Small and large Cu-Pt particles with a Cu/Pt ratio of 1:1 can be obtained through colloidal synthesis at 300 °C. The fresh particles have a Pt-rich surface and a Cu-rich core and can be converted into an intermetallic phase after annealing at 800 °C under H2. First, we demonstrated the stability of fresh particles under redox conditions at 400 °C, as the Pt-rich surface prevents substantial oxidation of Cu. Then, a combination of in situ scanning transmission electron microscopy, in situ X-ray absorption spectroscopy, and CO oxidation measurements of the intermetallic CuPt phase before and after redox treatments at 800 °C showed promising activity and stability for CO oxidation. Full oxidation of Cu was prevented after exposure to O2 at 800 °C. The activity and structure of the particles were only slightly changed after exposure to O2 at 800 °C and were recovered after re-reduction at 800 °C. Additionally, the intermetallic CuPt phase showed enhanced catalytic properties compared to the fresh particles with a Pt-rich surface or pure Pt particles of the same size. Thus, the incorporation of Pt with Cu does not lead to a rapid deactivation and degradation of the material, as seen with other bimetallic systems. This work provides a synthesis route to control the design of Cu-Pt nanostructures and underlines the promising properties of these alloys (intermetallic and non-intermetallic) for heterogeneous catalysis.

Preparation and Catalysis of Novel Colloidal Dispersions of Copper/Noble Metal Bimetallic Clusters

Preparation, characterization and catalyses of light-transition-metal/noble-metal bimetallic alloy nanoclusters

Novel Preparation, Characterization and Catalytic Properties of Polymer-Protected Cu/Pd Bimetallic Colloid.

Polymer-Protected Cu/Pd Bimetallic Clusters

High-performance Heterogeneous Catalysis with Surface-Exposed Stable Metal Nanoparticles.

Nanoscopic Naked Cu/Pd Powder as Air-Resistant Active Catalyst for Selective Hydration of Acrylonitrile to Acrylamide

Colloidal noble-metal and bimetallic alloy nanocrystals: a general synthetic method and their catalytic hydrogenation properties.

Preparation and Immobilization of Polymer-Protected Bimetallic Colloids

Coll 26-Colloid Chemistry Synthesis Of Metal Nanoparticle Catalysts

Facile Synthesis of Highly Dispersed and Well‐Alloyed Bimetallic Nanoparticles on Oxide Support

Concave Cu-Pd bimetallic nanocrystals: Ligand-based Co-reduction and mechanistic study

Facile Synthesis of Cu-Pd Bimetallic Multipods for Application in Cyclohexane Oxidation

A Facile Route To Monodisperse Mpd (M = Co Or Cu) Alloy Nanoparticles And Their Catalysis For Electrooxidation Of Formic Acid

Array-Based Clusters of Copper with Largely Exposed Metal Sites for Promoting Catalysis

Bimetallic Pd-Cu nanocrystals and their tunable catalytic properties.

Aerosol Spray Drying Guided Synthesis of Ultrasmall Alloyed Bimetallic Nanoparticles Supported on Silica for Catalytic Semihydrogenation

Synthesis and Characterization of Stable Cu-Pt Nanoparticles under Reductive and Oxidative Conditions

Preparation and Characterization of Polymer-Protected PtCo Bimetallic Colloids and Their Catalytic Properties in the Selective Hydrogenation of Cinnamaldehyde

Self-assembly Ultrathin Fe-BDC As Synergistic Catalytic Platforms for Selective Hydrogenation

Synthesis and Characterization of Cu-Pt Bimetallic Nanoparticles

Novel Powder-Supported Size-Selected Clusters for Heterogeneous Catalysis under Realistic Reaction Conditions