Abstract:Empirical wear transition maps have been constructed to delineate the load velocity conditions under which wear transitions occurred in an A356 AI alloy and an A356 Al20%SiC composite. Experiments were performed in dry sliding conditions, using a block-on-ring (SAE 52100) configuration, within a load range of 0.2–400 N and a sliding velocity range of 0.2–5.0 m s−1. Both materials displayed transitions from mild to severe wear at specific load and sliding velocity combinations. The mild wear regime for the composite was expanded to a higher range of sliding speeds and loads by comparison with unreinforced A356 Al. Within the mild regime, two sub-regimes existed for both materials, namely where mixing/oxidation occurred at low sliding speeds to produce a thermally insulating surface layer, and another at higher speeds where this layer was removed. In the composite an additional wear transition, i.e. from mild to ultra-mild regime, occurred at low loads and velocities where the wear rates of the composite were at least two orders of magnitude lower than unreinforced A356 Al, due to the load supporting effect of the particles at the contact surfaces. In both materials, the transition from mild to severe wear occurred at conditions where the surface (bulk) temperature exceeded a critical value of approximately 125 °C in the A356 Al and 338 °C for the composite. The temperature data were summarised in the form of surface temperature maps on log load versus log velocity axes.Wear mechanisms in each regime were determined using scanning electron microscopy, and energy dispersive spectroscopy techniques that were used to analyse morphologies, microstructures and chemical compositions of worm surfaces and wear debris. The dominant mechanisms in each regime were identified and correlated with wear rate and temperature map data to summarise the effects of reinforcement on wear rates and transitions.

Wear mechanism map of uncoated HSS tools during drilling die-cast magnesium alloy

Wear behavior of different coated tools in MQL-assisted high-speed milling of magnesium-based rare-earth alloys

Study on the Orthogonal Cutting Process of Al7050T7451 with Uncoated and Coated Tools

Research on Wear Mechanism of Coated HSS Drills during Machining Stainless Steel

The Wear Mechanism of the Chamber and Plunger Materials of Hot Chamber Die Casting Machine for Magnesium Alloy

Detecting Safety Zone Drill Process Parameters for Uncoated HSS Twist Drill in Machining GFRP Composites by Integrating Wear Rate and Wear Transition Mapping

Overview no. 55 Wear-Mechanism maps

The relevance of wear-mechanism maps to mild-oxidational wear

Wear mechanism maps for metal matrix composites

Modeling drill bit wear mechanisms during rock drilling

Multi-pattern failure modes and wear mechanisms of WC-Co tools in dry turning Ti–6Al–4V

Tool wear monitoring in drilling of high-strength compacted graphite cast irons

Simulation and experimental study of tool wear in high-speed dry gear hobbing

Research on Tool Wear in Machining of Particle Reinforced Aluminium Metal Matrix Composites Using PCD Tool

Friction Behavior and Self-Lubricating Mechanism of SLD-MAGIC Cold Worked Die Steel during Different Wear Conditions

Analysis of Tool Wear in GH4169 Material Milling Process

Tool wear mechanism of turning Inconel 718 and EEMD-based feature analysis

Study on tool wear in longitudinal-torsional composite ultrasonic vibration–assisted drilling of Ti-6Al-4V alloy

STUDY ON THE WEAR PERFORMANCES OF CERAMIC TOOLS FOR MACHINING 304 STAINLESS STEEL

Friction - wear modeling in drilling process of H-13 tool steel

Performance of High-Speed Steel Drills in Wet Drilling Inconel 718 Superalloy