Study on Preparation and Properties of Cross-Linking and Esterifying Starch of Mechanical Activated Cassava Starch
Chen Yuan,Yang Jiatian,Xie Zufang,Tan Yiqiu,Huang Zuqiang,Zhou Qin
DOI: https://doi.org/10.3969/j.issn.1003-0174.2012.12.007
2012-01-01
Abstract:Cross-linking and esterifying starch of mechanical activated cassava starch was prepared by using mechanical activated cassava starch as raw material,and using sodium trimetaphosophate for cross-linking agent and acetic anhydride for acetification,which its synthesis route prepared by continual reactions in one-step synthesis way.The effects of reaction temerature,cross-linking agent and esterifying agent dosage,pH value of cross-linking and esterifying and cross-linking time on the cold viscosity of cross-linking and esterifying starch paste were investigated respectively,and the physical and chemical Parameters and structure of the cross-linking and esterifying starch with mechanical activated cassava starch and cross-linking and esterifying starch with raw cassava starch were studied.The results indicated that the above reaction conditions were all found to affect the preparation of cross-linking and esterifying mechanical activated cassava starch.Under the reaction temperature 40 ℃,1.0% amounts of sodium trimetaphosphate,crosslinking pH value 10.0,crosslinking time 2.0 h,acetic anhydride amount 0.5 mL,esterifying pH value 9.0,esterifying time 60 min,the cold viscosity of cross-linking and esterifying starch paste of mechanical activated cassava was enhanced from 847 mPa.s of cassava starch to 3 225 mPa.s,and the stability,acidity-resistance,staling resistance of the viscosity of starch paste were significantly improved.Cross-linking and esterifying composite modified was propitious to formation of V type crystal starch.