Abstract:Co-based compounds have attracted much attention due to their competitive catalytic activities. To enhance their intrinsic electrocatalytic activity, morphology engineering is one of the effective strategies. Hollow structures have fascinating properties due to their low density and high loading capacity. In this work, we introduce a Ga-based liquid alloy as a reactive template for the synthesis of varying Co-based hollow nanoparticles. The fluidity character of the Ga-based liquid alloy facilitates the large-scale production of nanoparticles via a top-down shearing process. The pre-installed active species (here is Zn) in the liquid alloy serve as a sacrificial source to quantitatively reduce Co2+ ions and form Co-based compounds. Well-structured Ga/CoOOH core-shell nanospheres are thus successfully prepared, and more varied Co-based hollow nanoparticles can be obtained by post-treatment and reaction. Hollow structures can offer enhanced interfacial area and increased active sites, benefiting the catalytic performance. Among the prepared Co-based catalysts, CoSe2 hollow nanoparticles exhibited the best oxygen evolution reaction (OER) activity with an overpotential of 340 mV at the current density of 10 mA/cm2. This work provides a novel strategy for the rational design and simple preparation of hollow nanoparticles.

Controllable fabrication of monodisperse Co–B hollow microspheres

Hydrothermal Synthesis of Cobalt Particles with Hierarchy Structure and Physicochemical Properties

Microstructure Evolution and Magnetic Properties of Co–B Coatings Electrolessly Plated on Hollow Microspheres

A Facile Colloidal Templating Method to Monodisperse Hollow Ag and Ag/Au Submicrometer Spheres

Hydrothermal synthesis and characterization of core/shell ALOOH microspheres

Formation of Cobalt Hollow Nanospheres Via Surfactant-Assisted Hydrothermal Progress

One-pot synthesis and magnetic properties of hollow Fe<sub>70</sub>Co<sub>30</sub> nanospheres

Synthesis of Core–shell Α-Fe2o3 Hollow Micro-Spheres by a Simple Two-Step Process

A Facile Interfacial Reaction Route to Prepare Magnetic Hollow Spheres with Tunable Shell Thickness

Design and Synthesis of Cobalt-Based Hollow Nanoparticles through the Liquid Metal Template

Fabrication of Hollow (ni0.8co0.1mn0.1) [ozgur, 2010 #912]oy Spheres by Ultrasonic Spray Pyrolysis Method

A Facile Route to Synthesis of Ordered Arrays of Metal Nanoshells with A Controllable Morphology

A Facile Method to Prepare Monodispersed ZnO–Ag Core-Shell Microspheres

Use of Carbonaceous Polysaccharide Microspheres As Templates for Fabricating Metal Oxide Hollow Spheres

Fabrication of monodisperse CdS hollow spheres

Synthesis, Characterization and Magnetic Properties of Hollow Microspheres with Micro-Mesoporous Shells Assembled from Cobalt-Based Ferrocenyl Coordination Polymers

Tunable Co3O4 Hollow Structures (from Yolk–shell to Multi-Shell) and Their Li Storage Properties

Controlled fabrication of uniform hollow bowl-shaped microspheres based on polyphosphazene material

Facile approach for the fabrication of monodisperse hollow silica spheres

Nanoengineering of Core-Shell Magnetic Mesoporous Microspheres with Tunable Surface Roughness.

Cobalt oxide hollow microspheres with micro- and nano-scale composite structure: Fabrication and electrochemical performance