Few Layer g-C 3 N 4 Dispersed Quaternary Phosphonium Ionic Liquid for Highly Efficient Catalytic Oxidative Desulfurization of Fuel
Suhang Xun,Qiutong Ti,Linlan Wu,Minqiang He,Chao Wang,Linlin Chen,Wenshu Yang,Linhua Zhu,Wenshuai Zhu,Huaming Li
DOI: https://doi.org/10.1021/acs.energyfuels.0c02357
2020-09-22
Abstract:Functionalized ionic liquids (ILs) have been considered as efficient catalysts for oxidative desulfurization (ODS), but the further industrial applications are hampered by the poor separability with oil phase after reaction and large dosage. In this work, few-layered graphitic carbon nitride (g-C<sub>3</sub>N<sub>4</sub>) with high specific surface area was prepared via thermal oxidation and employed as a carrier to construct supported ionic liquid catalyst for ODS. A functional quaternary phosphonium ionic liquid [(C<sub>6</sub>H<sub>13</sub>)<sub>3</sub>PC<sub>14</sub>H<sub>29</sub>]<sub>3</sub>PMo<sub>12</sub>O<sub>40</sub> (abbreviated as C<sub>14</sub>PPMo) was synthesized and immobilized on g-C<sub>3</sub>N<sub>4</sub>. Then, the as-prepared samples were characterized by FT-IR, DRS, XRD, N<sub>2</sub> adsorption–desorption isotherm, XPS, SEM, and TEM, systematically. It was found that few layer g-C<sub>3</sub>N<sub>4</sub> had a large specific surface area (194.89 m<sup>2</sup> g<sup>–1</sup>), which was conducive to the high dispersion of C<sub>14</sub>PPMo IL. The obtained support catalyst C<sub>14</sub>PPMo/g-C<sub>3</sub>N<sub>4</sub> exhibited outstanding catalytic ability on the oxidation of dibenzothiophene (DBT), and the desulfurization efficiency could reach 100% with a small dosage of IL under optimal conditions. The oxidative products of DBT and 4,6-dimethyldibenzothiophene (4,6-DMDBT) were the homologous sulfones and proved by GC-MS, and the proposed reaction processes were studied, respectively. Since the supported IL was a heterogeneous catalyst and no additional solvent was added, C<sub>14</sub>PPMo IL could be separated and repossessed readily after the reaction. Moreover, the recycle ability of C<sub>14</sub>PPMo/g-C<sub>3</sub>N<sub>4</sub> on the oxidation of both DBT and 4,6-DMDBT were investigated simultaneously, and both of the desulfurization activities could still remain above 90% after 6 times cycling.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.0c02357?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.0c02357</a>.Material and methods, the cations and anions of functional ionic liquids for ODS (Scheme S1), FT-IR spectrum of 30% C<sub>14</sub>PPMo/g-C<sub>3</sub>N<sub>4</sub> (Figure S1), wide-angle XRD pattern of 30% C<sub>14</sub>PPMo/g-C<sub>3</sub>N<sub>4</sub> and 50% C<sub>14</sub>PPMo/g-C<sub>3</sub>N<sub>4</sub> (Figure S2), SEM image and EDS-mapping of 5% C<sub>14</sub>PPMo/g-C<sub>3</sub>N<sub>4</sub> (Figure S3), and the GC-MS analysis of catalyst phase after the reaction. (A) Oxidation of DBT and (B) oxidation of 4,6-DMDBT (Figure S4) (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.0c02357/suppl_file/ef0c02357_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
energy & fuels,engineering, chemical