Development of Thermal Barrier Coating with Fine Columnar Crystal Structure Fabricated by Supersonic Atmospheric Plasma Sprayed

Han Zhi-hai,Wang Hai-jun,Bai Yu,Ding Chun-hua,Xu Bin-shi

DOI: https://doi.org/10.3969/j.issn.1674-7127.2011.02.002

2011-01-01

Abstract:The recently investigation progress of the thermal barrier coating(TBC) with fine columnar grains was fabricated by a newly developed technology which was called supersonic atmospheric plasma spraying(SAPS).The in-flight rate of molten particles of 8% Y2O3 stabilized ZrO2 powders(8YSZ) with diameter 15~45μm for the heat insulated top ceramic coat in the SAPS jet was on-line monitored by means of SprayWatch-2i.The results display that the in-flight rate of molten particles was about 400～450 m/s,2～3 times higher than that in conventional APS stream(130～220 m/s),resulting in a remarkable finer microstructure for SAPS-TBCs.The volume fraction of finer lamella structure with columnar grains in SAPS-TBCs was above 80%,and their axial length of columnar grains were in the range of 2～5μm while the porosity of as-sprayed coating can be controlled from 1% to 12%.The unique microstructure of SAPS-TBCs was responsible for greatly improvement of their thermal cycling life.The thermal cycle number of SAPS-TBC specimens was above 400 cycles,2～3 times higher than that of conventional APS-TBCs(less than 150cyc.).In addition,the bonding strength of SAPS-TBCs was about 50MPa,over 65% higher than that of APS-TBCs(approximately 30MPa).Meanwhile,it was very interesting that the thermal insulation performance of SAPS-TBC rise with the increase of thermal cycles,while that of APS-TBCs descend with the increase of thermal cycles.And high temperature oxidation test on the fully coated samples at 1100℃ for 1000h demonstrated that SAPS-TBCs is beneficial to anti-oxidation as compared with APS-TBCs.Also,SAPS spraying process has the same advantages similar to the APS spraying process,such as easy operation process,lower cost and high efficiency etc.,so SAPS spraying technology will exhibit more important application in industry.