Liquid-Crystalline Polyethers Based on Conformational Isomerism .15. Smectic and Crystalline Phases in Copolyethers Based on 1,2-Bis(4-hydroxyphenyl)ethane and Combinations of 1,10-Dibromodecane with 1,12-Dibromododecane and of 1,8-Dibromooctane with 1,12-Dibromododecane

G UNGAR,JL FEIJOO,V PERCEC,R YOURD

DOI: https://doi.org/10.1021/ma00005a030

IF: 5.5

1991-01-01

Macromolecules

Abstract:The synthesis and characterization of copolyethers based on 1,2-bis(4-hydroxyphenyl)ethane (BPE) and a 1/1 molar ratio of 1,10-dibromodecane with 1,12-dibromododecane [BPE-10/12(1/1)] and, respectively, BPE and a 1/1 molar ratio of 1,8-dibromooctane with 1,12-dibromododecane [BPE-8/12(1/1)] are described. A combination of techniques consisting of differential scanning calorimetry (DSC), simultaneous X-ray diffraction/DSC (XDDSC), and thermal optical polarized microscopy was used for the characterization of both copolymers. BPE-10/12(1/1) exhibits two orthorhombic crystalline (Cr and Cr') phases and an enantiotropic smectic B phase (probably the crystal B variant). In the Cr phase the spacers are crystalline, while in the Cr' phase they are in a molten state. BPE-8/12(1/1) exhibits an enantiotropic smectic B phase and an enantiotropic hexagonal columnar mesophase. Fibers drawn from BPE-10/12(1/1) orient the plane of the smectic layer parallel to the draw direction, suggesting that a substantial fraction of polymer chains form reentrant folds within the spacer layer. This result is contrary to findings in previous main-chain liquid crystalline polymers where the plane of the smectic layer aligns perpendicular to the draw direction.