Structural Distortion-Induced Low-Temperature Dielectric Dispersion in Lanthanide Titanate Pyrochlores
Ming-Yuan Yan,Yu Xing,Xiao-Yu Zhang,Xing Li,Ao-Li Shen,Xin-Di Zhou,Meng Xu,Weiyao Zhao,Fei-Fei Wang,Shan-Tao Zhang
DOI: https://doi.org/10.1063/5.0223195
IF: 4
2024-01-01
Applied Physics Letters
Abstract:Rare-earth titanate pyrochlores have attracted significant attention for their unique magnetic frustration; however, research on the origin of low-temperature dielectric dispersion and the relationship between dielectric properties and structure lags far behind. Here, by systematically investigating the dielectric properties of representative rare-earth titanates R2Ti2O7 (R = La, Nd, Sm, Er, Yb, and Lu), we demonstrate that R2Ti2O7 with a cubic pyrochlore structure exhibits low-temperature dielectric dispersion behavior, while the other compounds with a monoclinic perovskite-like layered structure possess no dispersion behavior but excellent temperature-stable dielectric property. The dielectric dispersion in cubic pyrochlores arises from the structural distortion. Furthermore, the existence of structural distortion is affirmed by the anomalous phonon softening of A1g Raman mode around the dielectric dispersion temperature, and the origin of the structural distortion is attributed to anharmonic phonon–phonon interactions induced by intrinsic vacant oxygen at Wyckoff 8a sites. In addition, with increasing ionic radius from R = Lu to Sm, the increased lattice parameter leads to varied bond length and bond angle of Ti-O(1)-Ti, which strengthens the local lattice distortion of TiO(1)6 octahedra and thus enhances diffusion degree of dielectric dispersion. On the other hand, the absence of intrinsic vacant oxygen site hardly gives rise to the local structural distortion and thus no dielectric dispersion in monoclinic R2Ti2O7. Our work not only clarifies the mechanism of dielectric dispersion but also gives a comprehensive perspective on the structure–property relationship of rare-earth titanates R2Ti2O7, and thus lays a solid foundation for further work on related materials.