Enhanced absorption bandwidth in carbon-coated supermalloy FeNiMo nanocapsules for a thin absorb thickness
X.G. Liu,Z.Q. Ou,D.Y. Geng,Z. Han,H. Wang,B. Li,E. Brück,Z.D. Zhang
DOI: https://doi.org/10.1016/j.jallcom.2010.07.085
IF: 6.2
2010-01-01
Journal of Alloys and Compounds
Abstract:Research highlights ▶ Synthesis of carbon-coated FeNiMo nanocapsules. ▶ The special core/shell microstructure in the nanocapsules results in the low permittivity. The good match between high permeability and low permittivity result in outstanding EM-wave absorption properties of FeNiMo/C nanocapsules. ▶ The FeNiMo/C nanocapsules, synthesized by arc-discharging Fe 11 Ni 79 Mo 10 (at.%) alloy in ethanol, exhibited outstanding reflection loss (RL < −20 dB) in the range of 13–17.8 GHz with an absorber thickness of 1.7 mm, and an optimal RL of −64.0 dB was obtained at 13.2 GHz with an absorber thickness of 1.9 mm. The broadest bandwidth (RL < −10 dB) from 9 to 18 GHz, covering the whole Ku-band (12.4–18 GHz) and almost the whole X-band (9–12.4 GHz), was achieved for a 2 mm layer. Abstract Electromagnetic-wave absorption properties of FeNiMo/C nanocapsules with FeNiMo nanoparticles as cores and carbon as shells have been studied. The FeNiMo/C nanocapsules, synthesized by arc-discharging Fe 11 Ni 79 Mo 10 (at.%) alloy in ethanol, exhibited outstanding reflection loss (RL < −20 dB) in the range of 13–17.8 GHz with an absorber thickness of 1.7 mm, and an optimal RL of −64.0 dB was obtained at 13.2 GHz with an absorber thickness of 1.9 mm. The broadest bandwidth (RL < − 10 dB) from 9 to 18 GHz, covering the whole Ku-band (12.4–18 GHz) and almost the whole X-band (9–12.4 GHz), was achieved for a 2 mm layer. The excellent electromagnetic properties are ascribed to the good match between high permeability from the core of FeNiMo nanoparticles and low permittivity from the special core/shell microstructure in the FeNiMo/C nanocapsules. Keywords Nanocapsules Arc-discharge Electromagnetic wave absorption 1 Introduction In recent years, with the purpose of solving the expanded electromagnetic (EM) interference problems, it is highly desirable that reflection loss (RL) exceeding −20 dB in EM-wave absorption materials, which the RL value of −20 dB corresponds to 99% EM-wave absorption, spans over a wide frequency range for a thin absorb thickness. Magnetic nanocapsules (e.g., magnetic nanoparticles coated by dielectric layers) as new type of EM-wave absorption materials has attracted interest on account of the following facts: (1) compared with the traditional ferrites, the larger saturation magnetization ( M s ) leading to Snoek's limit at higher frequency. (2) The suppression of the eddy current enhancing an effective incidence to EM-wave, and (3) the combination of magnetic and dielectric materials in one nanocapsules, leading to effective interface between magnetic and dielectric materials [1–6] . Due to the interesting EM properties and the low density (∼1.76 g cm −3 ) of carbon, recent studies on nanocapsules with carbon as shells used as EM interference shielding and absorption materials have become more intensive [7–10] . Zhang and co-workers reported that carbon-coated Fe and Ni nanocapsules exhibit improved EM-wave absorption properties [1,2] . For carbon-coated Fe nanocapsules, an optimal reflection loss (RL) of −43.5 dB was reached at 9.6 GHz with an absorber thickness of 3.1 mm. The excellent EM-wave absorption properties are a consequence of a proper EM match in microstructure, a strong natural resonance, as well as multi-polarization mechanisms, etc. [2] . Han et al investigated the EM properties of FeCo/C nanocapsules [6] . In contrast to earlier reported materials, the absorption amplitude of FeCo/C nanocapsules was found not to decrease with increasing absorption-layer thickness. A RL exceeding −20 dB can be obtained for all frequencies within the 2–18 GHz range by choosing an appropriate layer thickness between 1.6 and 8.5 mm [6] . For EM-wave absorbers, the balance between complex permittivity ( ε γ = ε ′ γ − i ε ″ γ ) and permeability ( μ γ = μ ′ γ − i μ ″ γ ) is essential in determining the reflection and attenuation properties [3–6,11–13] . The impedance match between the absorbers and free space is required to achieve low reflection and full introduction of the EM-wave into the materials. Furthermore, according to the transmission line theory, the value of permittivity ( ɛ γ ) should be close to that of permeability ( μ γ ) in order to obtain the desired impedance match. For most of magnetic metals, the values of μ ′ γ are much smaller than those of ε ′ γ in the microwave band, so a lower permittivity and a higher permeability are required for absorbers. Compared with microscale counterparts, nanocapsules present relatively low permittivity values due to high resistivity and enhanced permeability for the increase in effective anisotropy. It is known that Ni–Fe alloys as a kind of important soft-magnetic materials have been widely applied in the field of electronic devices and industry, in which the permalloys with nominal composition Ni 81 Fe 19 (wt%) processes the highest permeability [14] . On the basis of high permeability of FeNi alloy and low permittivity of core/shell structured nanocapsules, carbon-coated FeNi alloy nanocapsules have been prepared by a modified arc-discharge technique in ethanol vapor [15] . RL exceeding −10 dB was obtained in the whole Ku-band (12.4–18 GHz) for an absorber thickness of 2.0 mm, while it exceeds −20 dB over the 13.6–16.6 GHz range. In addition, bandwidth does not change dramatically for the thicknesses of 1.87–2.1 mm for the RL values exceeding −10 dB [15] . The carbon-coated FeNi nanocapsules have improved the steadily of absorption ability. Supermalloy Ni 79 Fe 16 Mo 5 (wt%) has an improved loss characteristic over permalloy materials, which target a higher operating frequency [14] . However, as far as we know, there has been no report on the EM properties of carbon-coated FeNiMo alloy nanocapsules. Thinking about the higher permeability of supermalloy at high frequency, it is therefore conceivable that excellent EM-wave absorption properties could be achieved in nanocapsules with a core of FeNiMo alloy nanoparticles embedded in carbon layers. The purpose of this study is to prepare the carbon-coated FeNiMo alloy nanocapsules and to investigate the EM properties of these FeNiMo/C nanocapsules. It is found that the FeNiMo/C nanocapsules prepared by arc-discharging Fe 11 Ni 79 Mo 10 (at.%) alloy, exhibit outstanding EM-wave absorption properties. An optimal RL of −64.0 dB was obtained at 13.2 GHz with an absorber thickness of 1.9 mm. The broadest bandwidth (RL < − 10 dB) from 9 to 18 GHz, covering the whole Ku-band (12.4–18 GHz) and almost the whole X-band (9–12.4 GHz), was obtained for a 2 mm layer. In addition, the bandwidth (RL < −20 dB) exceeds 3 GHz and the bandwidth (RL < −10 dB) exceeds 6 GHz for the absorber thicknesses of 1.5–3.0 mm. 2 Experimental The modified arc-discharge method used in this work was described in detail elsewhere [15–17] . In brief, ingots of Fe 11 Ni 79 Mo 10 , Fe 16 Ni 79 Mo 5 and Fe 14 Ni 79 Mo 7 (at.%) alloys served as the anode, respectively, while the cathode was a carbon needle. The atomic proportions of the ingot based on their evaporation pressures and the composition of supermalloy. The anode target was placed into a water-cooled carbon crucible. After the chamber was evacuated in a vacuum of 5.0 × 10 −3 Pa, liquid ethanol of 40 ml was introduced into the chamber together with pure argon of 1.6 × 10 4 Pa and hydrogen of 0.4 × 10 4 Pa as a reactant gas and a source of hydrogen plasma. The arc-discharge current was maintained at 80 A for 2 h to evaporate alloys sufficiently. Then the products were collected from depositions on the top of the water-cooled chamber, after passivated for 8 h in argon. Three samples of the nanocapsules, prepared by arc discharging the Fe 11 Ni 79 Mo 10 , Fe 16 Ni 79 Mo 5 and Fe 14 Ni 79 Mo 7 alloys, were denoted as samples A, B and C, respectively. Phase analysis of the products was performed by powder X-ray diffraction (XRD) on a Rigaku D/max-2000 diffractometer at a voltage of 56 kV and a current of 182 mA with graphite monochromatized Cu-K α ( λ = 0.154056 nm) radiation. The morphology of the nanocapsules was studied in a high-resolution transmission electron microscope (HRTEM JEOL-2010) with an emission voltage of 200 kV. Quantitative analysis of the elements present in the as-prepared products was performed by means of energy dispersive spectroscopy (EDS). For measuring the EM parameters, i.e., the complex permittivity ɛ γ and permeability μ γ , the nanocapsules were homogeneously mixed into a paraffin matrix and compressed into a cylindrical compact. First of all, paraffin wax was melted and nanocapsules were dispersed randomly into the paraffin wax with a mass ratio of 2:3. The blend was then mechanically stirred for 1 h. Finally, the nanocapsules-paraffin mixture was pressed into a toroidal cylinder with 3.04 mm in inner diameter and 7.00 mm in outer diameter for further testing. The paraffin matrix is an EM-wave transparent material, so the EM parameters obtained are mostly from the nanocapsules. The ɛ γ and μ γ of the nanocapsules-paraffin composites were determined with the transmission and reflection coaxial line method. To ensure the precision of the measurements, full two-port calibration was initially performed on the test setup to remove errors caused by the directivity, source match, load match, isolation, and frequency response in both the forward and reverse measurements [18] . In the range of 2–18 GHz, the scattering parameters ( S 11 and S 21 ) were measured by an Agilent 8722ES vector network analyzer. The ɛ γ and μ γ were determined from the scattering parameters using the Nicolson–Ross (for magnetic) and precision (for nonmagnetic) models [18,19] . 3 Results and discussion In Fig. 1 , XRD patterns show the phase components of the nanocapsules (samples A–C) prepared by arc-discharging Fe–Ni–Mo alloys with different composition in ethanol vapor. All sharp reflection peaks could be indexed with the FeNi-type structure. However, they are called FeNiMo alloy nanocapsules on the basis of EDS results ( Table 1 ) and XRD peak shift. No reflection for oxides could be found, indicating that FeNiMo nanoparticles are almost without oxidation, due to the protective carbon shell [1] . In the XRD patterns, there are no detectable peaks for pure carbon, indicating its small amount (less than 3% in the samples). Furthermore, since carbon is on the shell of the nanocapsules, it is also difficulty to detect its XRD pattern because of breaking down of the periodic boundary condition (translation symmetry) along radial direction. The morphology of sample A can be observed clearly in Fig. 2 (a) . Most of the as-prepared nanocapsules are of irregular sphere shape. It is understood that the lower-energy state for the crystallization processes dominates the concrete morphology of the carbon-coated FeNiMo nanocapsules [20] . As measured from TEM observations, the size of the nanocapsules ranges from 10 to 80 nm and the average size is 32.1 nm and the shell thickness is 4.5 nm for sample A. The HRTEM image, as shown in Fig. 2 (b), clearly indicates that a nanocapsule owns a ‘core/shell’ type structure and the inner FeNiMo alloy cores are encapsulated into the onion-like carbon cages. The lattice plane spacing of the coating layers is about 0.34 nm, which corresponds to the (0 0 2) plane of graphite. Nevertheless, a lot of lattice imperfections can be seen in the outer shells as a consequence of the serious bending and collapsing of the graphite atom layer, which is similar with the Fe/C and FeNi/C nanocapsules [1,15] . In addition, the graphite shell of the carbon-coated FeNiMo nanocapsules prepared in ethanol vapor is thinner than that of Fe/C and Ni/C nanocapsules prepared in CH 4 , which is ascribed to the lower carbon content in ethanol [15,16] . The particle size distribution, average diameter, shell thickness and composition of the FeNiMo/C nanocapsules (samples A–C), as measured from TEM observation and EDS results and the composition of their master alloys, are presented in Table 1 . In Table 1 , the difference between the compositions of the starting FeNiMo alloys and the as-prepared nanocapsules is displayed. This difference can be ascribed to the formation mechanism of the nanocapsules, i.e., different evaporating pressures, melting points for iron, nickel and molybdenum atoms, during the arc-discharging process. For an evaporating pressure of 133 Pa (1 Torr), the corresponding evaporating temperatures are 1537 °C for Fe, 1907 °C for Ni and 3117 °C for Mo. The melting points of iron, nickel and molybdenum are 1495, 1453 and 2617 °C, respectively. In the arc-discharge process, mainly iron and nickel atoms will evaporate and then collide in the gas phase to condenses first to the solid state, but a small amount of molybdenum atoms evaporate into the FeNi phase as solid-solution atoms [20] . The decomposition of ethanol vapor, due to the high temperature in the arc-discharge process, provides sufficient carbon atoms to form carbon shells on the surface of FeNiMo nanoparticles during the solidification process. Combining with the atomic proportions measured by EDS and atomic weight, it is noted that the composition of nanocapsules in sample A is very close to the supermalloy Ni 79 Fe 16 Mo 5 . It is observed that the samples A–C process the same size distribution of nanocapsules, due to the same experimental parameters during the arc-discharge process. The difference in the average diameter and shell thickness is ascribed to the evaporation of different elements and the sorption of nanoparticles with different size during the arc-discharge. Since the EM properties of the nanoparticles essentially depend on their size and especially on the core/shell proportion [1–7] , the different particle size and shell thickness indicate different EM-absorptive properties in samples A–C. Fig. 3 shows the frequency dependence of ɛ γ and μ γ of nanocapsules-paraffin composites. As seen in Fig. 3 (a), there is a similar tendency of the real part ( ε ′ r ) and the imaginary part ( ε ″ r ) of ɛ γ in samples A–C, due to the similar microstructure in nanocapsules. The values of ε ′ r decreases with increasing frequency in the 2–18 GHz range, while the values of ε ″ r exhibit a significant fluctuation, over the 2–18 GHz range, ascribed to the displacement current lag at the ‘core/shell’ interface [2] . Compared with the microscale metal-particles composites (for α-Fe particles, ε ′ r = 230 and ε ″ r = 400 ) [21] , the present nanocapsules have much lower permittivity, indicating a higher resistance. This is ascribed to the following fact: the graphite layers, in which the electrical resistivity is increased from the special microstructure and defect properties when thickness is in several nanometres, block the formation of an electric conducting network, which can contribute to low polarization and dielectric loss [18] . However, the differences in the permittivity values of samples A–C in the whole 2–18 GHz range indicate a higher electrical resistivity of the samples A, which comes from the smaller particles’ sizes and thicker shell. In general, a high electrical resistivity is good for improving the EM-wave absorption properties. The real part ( μ ′ r ) and the imaginary part ( μ ″ r ) of μ γ for samples A–C show almost the same variation in the 2–18 GHz range. μ ′ r values decrease with frequency in the 2–9 GHz range and retain almost constant from 9 to18 GHz, while μ ″ r exhibit broad multi-resonance peaks at about 2–9 GHz, which implies that natural-resonance occurs in the FeNiMo/C nanocapsules. It can be speculated that the multi-resonance peaks, as shown in Fig. 3 (b), are a consequence of the small size effect, surface effect and spin wave excitations, which have been defined as ‘exchange mode’ resonance [22,23] . Compared with the bulk FeNiMo, the natural-resonance frequency ( f r ) of the FeNiMo nanoparticles has been remarkably shifted to higher frequency, which is ascribed to the considerable increase of the surface anisotropy field ( H eff ) due to the size effect. These multi-resonance phenomena have also been analyzed in detail in recent investigation [2–6] . The similar variation in μ ′ r and μ ″ r arises from the same size distribution and similar average diameter and shell thickness for samples A–C. Compared with samples B and C, sample A processes higher values of μ ′ r and μ ″ r , which can be explained by the fact that the composition of nanocapsules is very close to that of the supermalloy, leading to high μ r in the GHz range. Generally, excellent EM-wave absorption results from efficient complementarities between the relative permittivity and permeability in materials [3–5] . To further prove the EM-wave absorption properties, the RL values of composites with different absorptive thicknesses were calculated in the range of 2–18 GHz, as shown in Fig. 4 , according to the transmit-line theory, by using the experimental data of relative complex permeability and permittivity [15,16] . The RL of EM-absorptive materials measured in decibel (dB) greater than −20 dB (note that −20 dB corresponds to 99% EM-wave absorption), should be adequate. From the view of applications, the absorbing ability (e.g., wide frequency range, strong absorption, etc.) must be improved for EM-wave absorbers, in which the upper limit of absorbing thickness is selected as 3 mm. As shown in Fig. 4 (a), an optimal RL of −64.0 dB was obtained at 13.2 GHz with an absorber thickness of 1.9 mm. For the absorber thickness of 1.7 mm, the broadest bandwidth (RL < −20 dB) is achieved in the range of 13–17.8 GHz that is broader than that reported previously for a single thickness [1–15] . The broadest bandwidth for RL < − 10 dB (note that −10 dB corresponds to about 70% EM-wave absorption) from 9 to 18 GHz, covering the whole Ku-band (12.4–18 GHz) and almost the whole X-band (9–12.4 GHz), was obtained for a 2 mm layer. In addition, the bandwidth (RL < −20 dB) exceeds 3 GHz and the bandwidth (RL < −10 dB) exceeds 6 GHz for the absorber thicknesses of 1.5–3.0 mm. Compared with samples B and C, the sample A exhibits larger optimal RL value, broader bandwidth (for both RL < −20 dB and RL < −10 dB). According to the transmission line theory, as the value of permittivity is close to that of permeability, one can obtain the desired impedance match. Compared with samples B and C, the sample A presents a lower permittivity and higher permeability. The smaller average size and thicker shell lead to lower polarization and dielectric loss, which make permittivity low. The composition of FeNiMo cores is very close to the composition of supermalloy, which leads to a higher permeability at the GHz range. The excellent EM-absorptive properties of the sample A come from the good match between high permeability from the FeNiMo nanoparticles and low permittivity from the special core/shell microstructure in the FeNiMo/C nanocapsules. 4 Conclusion In summary, the carbon-coated FeNiMo nanocapsules have been prepared by the arc-discharge technique in ethanol vapor. The phase, composition and microstructure of the FeNiMo/C nanocapsules have been investigated by means of XRD, EDS and HRTEM. The FeNiMo/C nanocapsules own a ‘core/shell’ type structure and the inner FeNiMo alloy nanoparticles as cores are encapsulated into the onion-like carbon cages as shells. The composition of as-prepared FeNiMo/C nanocapsules by arc-discharging Fe 11 Ni 79 Mo 10 (at.%) is very close to the supermalloy Ni 79 Fe 16 Mo 5 , which leads to the high permeability at the GHz range. The special core/shell microstructure in the nanocapsules results in the low permittivity. The good match between high permeability and low permittivity result in outstanding EM-wave absorption properties of FeNiMo/C nanocapsules. An optimal RL of −64.0 dB was obtained at 13.2 GHz with an absorber thickness of 1.9 mm. For the absorber thickness of 1.7 mm, the bandwidth (RL < −20 dB) is achieved in the range of 13–17.8 GHz that is broader than that reported previously for a single thickness. The broadest bandwidth (RL < − 10 dB) from 9 to 18 GHz, covering the whole Ku-band and almost the whole X-band, was obtained for a 2 mm layer. In addition, the bandwidth (RL < −20 dB) exceeds 3 GHz and the bandwidth (RL < −10 dB) exceeds 6 GHz for any absorber thicknesses in the range of 1.5–3.0 mm. The results suggest that the FeNiMo/C nanocapsules with wide bandwidth absorption are excellent EM-wave absorption materials. Acknowledgments This work has been supported partly by the Scientific Exchange Program between China and the Netherlands, partly by the National Basic Research Program (No. 2010CB934603) of China, Ministry of Science and Technology of China, and partly by the National Natural Science Foundation of China under Grant No. 50831006 and 50701045. References [1] X.F. Zhang X.L. Dong H. Huang Y.Y. Liu W.N. Wang X.G. Zhu B. Lv J.P. Lei C.G. Lee Appl. Phys. Lett. 89 2006 053115 [2] X.F. Zhang X.L. Dong H. Huang Y.Y. Liu B. Lv J.P. Lei C.J. Choi J. Phys. D: Appl. Phys. 40 2007 5383 5387 [3] X.G. Liu D.Y. Geng H. Meng P.J. Shang Z.D. Zhang Appl. Phys. Lett. 92 2008 173117 [4] X.G. Liu D.Y. Geng Z.D. Zhang Appl. Phys. Lett. 92 2008 243110 [5] X.G. Liu J.J. Jiang D.Y. Geng Z. Han W. Liu Z.D. Zhang Appl. Phys. Lett. 94 2009 053119 [6] Z. Han D. Li H. Wang X.G. Liu J. Li D.Y. Geng Z.D. Zhang Appl. Phys. Lett. 95 2009 023114 [7] J.R. Liu M. Itoh T. Horikawa M. Itakura N. Kuwano K. Machida J. Phys. D: Appl. Phys. 37 2004 2737 2741 [8] R.C. Che L.M. Peng X.F. Duan Q. Chen X.L. Liang Adv. Mater. 16 2004 401 405 [9] A. Wadhawan D. Garrett J.M. Perez Appl. Phys. Lett. 83 2003 2683 2685 [10] R.T. Lv F.Y. Kang J.L. Gu X.C. Gui J.Q. Wei K.L. Wang D.H. Wu Appl. Phys. Lett. 93 2008 223105 [11] J. Ma J.G. Li X. Ni X.D. Zhang J.J. Huang Appl. Phys. Lett. 95 2009 102505 [12] Y.J. Chen P. Gao C.L. Zhu R.X. Wang L.J. Wang M.S. Cao X.Y. Fang J. Appl. Phys. 106 2009 054303 [13] X.L. Shi M.S. Cao J. Yuan X.Y. Fang Appl. Phys. Lett. 95 2009 163108 [14] J. Füzer P. Kollár D. Olekšáková S. Roth J. Alloy Compd. 483 2009 557 559 [15] X.G. Liu B. Li D.Y. Geng F. Yang Z.D. Zhang Carbon 47 2009 470 474 [16] X.G. Liu Z.Q. Ou D.Y. Geng Z. Han Z.G. Xie Z.D. Zhang J. Phys. D: Appl. Phys. 42 2009 155004 [17] X.G. Liu D.Y. Geng Q. Zhang J.J. Jiang W. Liu Z.D. Zhang Appl. Phys. Lett. 94 2009 103104 [18] B. Lu H. Huang X.L. Dong X.F. Zhang J.P. Lei J.P. Sun C. Dong J. Appl. Phys. 104 2008 114313 [19] A.N. Yusoff M.H. Abdullah S.H. Ahmad S.F. Jusoh A.A. Manso S.A.A. Hamid J. Appl. Phys. 92 2002 876 882 [20] D.Y. Geng Z.D. Zhang W.S. Zhang P.Z. Si X.G. Zhao W. Liu K.Y. Hu Z.X. Jin X.P. Song Scr. Mater. 48 2003 593 598 [21] S.S. Kim S.T. Kim Y.C. Yoon K.S. Lee J. Appl. Phys. 97 2005 10F905 [22] D. Mercier J.C.S. Lévy G. Viau F.F. Vincent F. Fiévet P. Toneguzzo O. Acher Phys. Rev. B 62 2000 532 544 [23] A. Aharoni J. Appl. Phys. 81 1997 830 833
What problem does this paper attempt to address?
-
Broadband Electromagnetic-Wave Absorption by FeCo/C Nanocapsules
Z. Han,D. Li,H. Wang,X. G. Liu,J. Li,D. Y. Geng,Z. D. Zhang
DOI: https://doi.org/10.1063/1.3177067
IF: 4
2009-01-01
Applied Physics Letters
Abstract:Electromagnetic-wave absorption by FeCo/C nanocapsules has been investigated. In contrast to earlier reported materials, including other nanocapsules, the absorption amplitude of FeCo/C nanocapsules is found not to decrease with increasing absorption-layer thickness. A reflection loss (RL) exceeding −20 dB can be obtained for all frequencies within the 2–18 GHz range by choosing an appropriate layer thickness between 1.6 and 8.5 mm. The broadest bandwidth (RL values exceeding −10 dB) from 10 to 18 GHz, covering half of the X-band and the whole Ku-band, is obtained for a 2 mm layer.
-
Hollow FeNi/NiFe 2 O 4 -Codoped Carbon Composite Nanorods for Electromagnetic Wave Absorption
Hui-Min Wen,Hongdu Jin,Jiannan Pan,Qu Hong,Huipeng Lv,Bo Xie,John Q. Xiao,Jun Hu
DOI: https://doi.org/10.1021/acsanm.1c03972
IF: 6.14
2022-03-17
ACS Applied Nano Materials
Abstract:Electromagnetic wave absorbers (EMWAs) with light weight, strong absorption, broad absorption width, and thin thickness are in high demand. Metal–organic frameworks are considered to be an emerging type of ideal sacrificial precursor to synthesize multicomponent magnetic nanoparticles/porous carbon composites. Most of these multicomponent composites exhibit brilliant electromagnetic-wave-absorbing performances because of multifarious absorption mechanisms and better impedance matching. In this work, hollow spindle-shaped FeNi/NiFe2O4-doped carbon composite nanorods, denoted as FeNiC, were synthesized by one-step calcination of FeNi bimetallic MIL-101 at 600, 700, and 800 °C. A strong reflection loss (RL) of −62.7 dB and a broad effective absorption bandwidth (Δfe) of 7.46 GHz (12.4–18 GHz) covering the entire Ku band were optimized through control of the calcination temperature and thickness of paraffin wax. The remarkable EMWA performance was mainly attributed to the synergistic effect of hierarchical pores, geometric structure, and dielectric and magnetic losses. This work may provide an inspiring method to integrate multiple components and hierarchically porous structures to achieve lightweight and broadband EMWAs.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsanm.1c03972.XRD patterns of the FeNi-MIL-101 composites, SEM images of FeNiC-600 and FeNiC-800, HRTEM images, XPS spectra for the FeNiC-600 and FeNiC-800 composites, N2 adsorption–desorption isotherms, Cole–Cole plots, 3D plots of the relative input impedance, and relationship between the thickness and peak frequency derived from the quarter-wavelength cancellation model of the samples (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology
-
Tailoring of electromagnetic properties of arc-produced carbon-coated FeNi alloy nanocapsules for highly efficient microwave absorption
Xinghao Qu,Muhammad Javid,Xiyang Li,Feirong Huang,Pu Li,Yuping Duan,Zhidong Zhang,Xuefeng Zhang,Xinglong Dong
DOI: https://doi.org/10.1016/j.diamond.2023.110487
IF: 3.806
2023-12-01
Diamond and Related Materials
Abstract:Due to the growing harm of electromagnetic radiation, it is extremely urgent to develop high-efficiency microwave absorbers with tunable electromagnetic properties. Herein, a simple strategy for synthesizing hetero-atoms (sulfur) doped carbon-coated FeNi alloy nanocapsules (FeNi@C(S x ) NCs) by DC arc-discharge plasma was demonstrated. The hetero-interface between the FeNi alloy core and the graphitic shell induce interfacial polarization was found. Meantime, many defects produced by substitutional sulfur atoms in the graphitic shell facilitated dipole polarization and conduction loss. Besides, the multiple magnetic resonance produced by FeNi magnetic alloys worked together to optimize impedance matching. The excellent microwave absorption performance was attributed to the core-shell structure, dipole and interface polarizations, as well as favorable impedance matching. Importantly, the first-principles calculation was applied to prove the charge transfer and polarization process. The minimum reflection loss (RL) can reach up to −50.3 dB at a thickness of 1.6 mm.
materials science, multidisciplinary,physics, applied, condensed matter, coatings & films
-
Enhanced broadband microwave absorption of Fe/C core-shell nanofibers in X and Ku bands
Shixiang Dong,Jing Li,Ning Li,Shuai Zhang,Bo Li,Qianli Zhang,Liqin Ge
DOI: https://doi.org/10.1016/j.ceramint.2022.10.342
IF: 5.532
2023-03-01
Ceramics International
Abstract:Fe/C core-shell nanofibers were prepared via a coaxial electrospinning technique integrated with high-temperature carbonization, in which the Fe(NO3)3-containing PAN solution and Fe(NO3)3 constituted the shell and core structures, respectively. The core-shell structure was perfectly maintained after carbonization, and Fe nanoparticles were uniformly distributed within the carbon nanofibers. The effects of the microscopic morphology and crystallinity of the carbon components on the electromagnetic properties, matching characteristics, and electromagnetic wave absorption properties of the Fe/C nanofibers were investigated by adjusting the carbonization temperature. As-prepared Fe/C-800 °C core-shell nanofibers mixed with 10 wt% of paraffin showed a minimal reflection loss (RLmin) of −20.6 dB under 11.52 GHz at 2.5 mm of thickness and lower than −20 dB under 2.3–5.0 mm of thickness. The efficient absorption bandwidth (EAB) was 6.24 GHz in the range of 11.76–18 GHz at 2.1 mm, covering the whole Ku band. The absorption bandwidth can cover the whole X and Ku bands by varying the sample thickness. The efficient absorption bandwidth was 3.84 GHz in the range of 8.08–11.92 GHz at 2.9 mm, covering the X band. The effective complementarities between the magnetic loss of Fe nanoparticles, the dielectric loss of PAN-based carbon, and the core-shell structure promoted impedance matching and multiple interface polarization, endowing the produced composites with prominent absorption characteristics of microwaves. Therefore, the prepared Fe/C core-shell nanofibers are an ideal lightweight and broadband electromagnetic wave (EMW)-absorbing material that exhibits high-performance microwave absorption.
materials science, ceramics
-
Microwave-Absorption Properties of Fe(Mn)/Ferrite Nanocapsules
Zheng Han,Da Li,Xianguo Liu,Dianyu Geng,Ji Li,Zhidong Zhang
DOI: https://doi.org/10.1088/0022-3727/42/5/055008
2009-01-01
Abstract:Electromagnetic ( EM) wave absorption properties of the paraffin-Fe(Mn)/ferrite nanocapsule composite ( with 40 wt% nanocapsules) were investigated in the 2-18 GHz frequency range. The Fe(Mn)/ferrite nanocapsules synthesized by arc-discharging have a core-shell structure with cores 10-30 nm in diameter and shells about 5 nm in thickness. The reflection loss (RL) calculated from the measured permittivity and permeability was found to exceed -20 dB in the 13-15 GHz range for a thickness of about 1.75-1.95 mm. The optimal RL is -28.2 dB at about 14 GHz with 1.84mm thickness. RL values exceeding -10 dB were obtained for the absorber of 1.7mm thickness in the range 12.7-17.1 GHz, which almost covered the whole Ku-band (12.4-18 GHz). The excellent EM wave absorption properties of the Fe(Mn)/ferrite nanocapsules significantly depend on the core-shell microstructure and the match of dielectric and magnetic losses.
-
Ni nanospheres coated with tunable carbon shells for dielectric-controlled superior electromagnetic wave absorbing
Na Chen,Xin-Yi Wang,Dong Zhang,Dan Li,Zhen-Jie Guan,Jian-Tang Jiang,Kang-Jun Wang
DOI: https://doi.org/10.1016/j.mtcomm.2022.104507
IF: 3.8
2022-09-25
Materials Today Communications
Abstract:To obtain high-efficiency electromagnetic wave absorbing (EMA) materials with strong reflection loss ( RL ) and wide effective absorption bandwidth (EAB), Ni particles are successfully prepared in this work by a liquid phase reduction method, and is subsequently designed and fabricated through combined polymerization and carbonization process. The pristine Ni exhibits outstanding EMA performances in middle- and high-frequency with a maximum RL ( RL max ) of 62.3 dB (2.3 mm) at K u band and an EAB of 10.9 GHz (5.6–16.5 GHz) at 3.0 mm, covering 75 % K u (12–18 GHz), 100 % X (8–12 GHz) and 60 % C (4–8 GHz) band. Such a superior performance is attributed to the dielectric loss derived from interface polarization, dipole polarization and conduction loss, along with magnetic loss comes from natural and exchange resonance. The introducing of carbon shells with manipulated thicknesses induce positive enhancement in dielectric loss. Meanwhile, core-shell structures enable multiple scattering and reflection of microwaves. Thus, spheres exhibit significantly enhanced EMA performances in low-frequency covering S (2–4 GHz) and C band with an RL max at 4.4 GHz reaching 64.4 dB () and an RL max at 2.6 GHz reaching 59.3 dB (). Therefore, Ni and demonstrate a unique blend of favorable EMA performances, which is promising for the next-generation intelligent EMA systems.
materials science, multidisciplinary
-
The Electromagnetic Wave Absorption Properties Of Feni(3) Nanospheres And Feni(3)@C Nanocapsules
S. J. Yan,L. Zhen,C. Y. Xu,J. T. Jiang,W. Z. Shao
DOI: https://doi.org/10.1109/aps.2010.5561728
2010-01-01
Abstract:FeNi(3) nanospheres (NS) with an average diameter of 400 nm were synthesized by a simple low temperature reduction method. FeNi(3)@C core-shell structured nanocapsules (NC) were then fabricated with a hydrothermal process. The electromagnetic (EM) properties of paraffin matrix composites containing FeNi(3) NS and FeNi(3)@C NC were studied at 2-18 GHz. The effect of dielectric carbon coating on the EM properties and electromagnetic wave absorbing (EMA) performance was directly observed.
-
Synthesis and Microwave Electromagnetic Properties of CoFe Alloy Nanoflakes Prepared with Hydrogen-Thermal Reduction Method
Y. X. Gong,L. Zhen,J. T. Jiang,C. Y. Xu,W. Z. Shao
DOI: https://doi.org/10.1063/1.3211987
IF: 2.877
2009-01-01
Journal of Applied Physics
Abstract:CoFe alloy nanoflakes (NFs) with diameter and thickness on nanoscale were prepared by hydrogen-thermal reduction in CoFe2O4 flakes at 400 °C for 60 min. The effective complex permittivity and permeability of CoFe alloy NFs/paraffin composites were measured and compared with that of CoFe alloy nanoparticles (NPs)/paraffin composites. Due to the two-dimensional shape character, the real part of permittivity and permeability of CoFe alloy NFs was rather higher than that of CoFe alloy NPs. Electromagnetic wave absorbing (EMA) performance of both CoFe alloy NFs and NPs was evaluated by using transmission line theory. The effective EMA band position of the coating with CoFe alloy NFs as fillers was found to locate in the range of 2–4 GHz, while the effective EMA band position of the coating containing CoFe alloy NPs as fillers was located in the range 8–18 GHz. A maximum reflection loss (RLmax) of −57.8 dB was achieved in a coating containing CoFe alloy NFs as fillers, which is much higher than the −16.6 dB of ...
-
Carbon-encapsulated Co 7 Fe 3 nanocomposites with high intensity and ultra-wideband microwave absorption
Baolei Wang,Yonggang Fu,Jing Li,Tong Liu
DOI: https://doi.org/10.1016/j.carbon.2022.11.027
IF: 10.9
2022-11-16
Carbon
Abstract:Composites composed of ferromagnetic alloy/dielectric material have been widely studied and applied. The alloying of the two metals endows these composites with escalated magnetic loss capacity, but they are usually micro-sized, which is not conducive to further improving the absorption performance. Herein, we develop an efficient approach to synthesize Co 7 Fe 3 @C nanocomposites with particle sizes ranging from 32 to 42 nm based on the in-situ carbon coating on the FeCo 2 O 4 precursor and subsequent carbothermal reduction procedure. The thickness of carbon coating can be effectively tailored by controlling the reaction conditions. The minimum reflection loss (RL) value of the Co 7 Fe 3 @C nanocomposite with a carbon coating of 2.5 nm goes up to −100.8 dB at only 1.7 mm thickness, and the effective absorption bandwidth (EAB) also reaches 9.9 GHz (8.1–18 GHz) at 2.0 mm. Moreover, as the carbon coating increases to 4.2 nm, the bandwidth escalates to 11.5 GHz (6.5–18 GHz) at 2.0 mm, which covers the whole X and Ku bands and half of the C band. The remarkable performance originates from the strong magnetic loss capability of the nano-sized Co 7 Fe 3 core as well as the good impedance matching brought by appropriate carbon coating. Accordingly, the Co 7 Fe 3 @C nanocomposite is convinced to be a competent candidate among absorbers with high absorption intensity and ultra-wide broadband.
materials science, multidisciplinary,chemistry, physical
-
NiCo Alloy/Carbon Nanorods Decorated with Carbon Nanotubes for Microwave Absorption
Lei Wang,Bo Wen,Xiaoyu Bai,Chao Liu,Haibo Yang
DOI: https://doi.org/10.1021/acsanm.9b01842
IF: 6.14
2019-01-01
ACS Applied Nano Materials
Abstract:Fabricating high-performance electromagnetic absorbents with strong absorbing intensity and wide effective absorbing bandwidth at low filler loading is still a challenge. Herein, hierarchical NiCo alloy/carbon nanorod@carbon nano tube (NiCo alloy/carbon nanorod@CNT) structures were prepared by a carbonization process using NiCo-MOF-74 nanorods as precursors in Ar flow, in which the aspect ratio of the NiCo alloy/carbon nanorod and the coating density of the CNTs could be easily controlled by the ratio of Ni/Co in the precursor. When the Ni/Co molar ratio was 1:1, a dual electric network was easily formed among the NiCo alloy/carbon nanorods as well as between the intertwined coating CNTs due to the higher aspect ratio and larger coating density, which induced significant enhancement of the comprehensive microwave absorbing properties of the NiCo alloy/carbon nanorod@CNT composites. By adding only 5 wt % to paraffin, the resulting composite displayed a maximum reflection loss of -58.8 dB and a covered an effective bandwidth as wide as 6.5 GHz (11.5-18 GHz) with a matching thickness of 2.6 mm. These outstanding microwave absorption properties can be ascribed to the stronger microwave attenuation capacity caused by the dual electric network for extra conduction loss and better impedance matching. This work provides a new direction for the design of carbon-based absorber with high performance at low filler loading.
-
Binary and ternary ferromagnetic alloy/C nanocapsules for improved X-band microwave absorption
Sibt ul Hassan,Yang Yang,Daitao Kuang,Tauqeer Haidar Qamar,MinMing Zai,Sana Zafar,Lizhen Hou,Shiliang Wang
DOI: https://doi.org/10.1088/1361-6463/ad3f2b
2024-04-17
Journal of Physics D Applied Physics
Abstract:The dielectric-magnetic matching effect emerges from the presence of dual dielectric relaxation and multiple magnetic resonances. This phenomenon becomes a strategic approach in the quest to enhance microwave absorption (MA) performance by optimizing magnetic components. Herein, binary and ternary ferromagnetic alloy with tunable components embedded in carbon skeleton (core/shell) nanocapsules has been successfully fabricated by one step metal-organic chemical vapor deposition (MOCVD). The core/shell structure design introduces numerous interfaces that amplify dielectric loss stemming from polarization. It is important to emphasize that modifying the composition of magnetic core in these nanocapsules effectively regulates the impedance matching characteristics. As a result, the CoFeNi/C nanocapsules demonstrate an optimal reflection loss (RLmin) of -53.6 dB at a thickness of 2.55 mm, alongside an effective absorption bandwidth (EAB) of 5.92 GHz at a thickness of 2.05 mm, with a filling ratio as low as 20 wt%. This study has provided valuable insights into a promising avenue for fabricating dielectric-magnetic nanocomposites with outstanding microwave attenuation capabilities through the manipulation of composited elements.
physics, applied
-
Optimal Electromagnetic-Wave Absorption By Enhanced Dipole Polarization In Ni/C Nanocapsules
Han Wang,Huaihong Guo,Yingying Dai,Dianyu Geng,Zheng Han,Da Li,Teng Yang,Song Ma,Wei Liu,Zhidong Zhang
DOI: https://doi.org/10.1063/1.4747811
IF: 4
2012-01-01
Applied Physics Letters
Abstract:Electromagnetic-wave (EMW) absorption by Ni/C nanocapsules with similar permeability but different permittivity mainly due to differences in the graphite-shell thickness has been investigated. The optimal working frequency could appear at S-band and C-band and considerable strong EMW absorption was achieved. For the optimal Ni/C nanocapsules, a reflection loss exceeding -20 dB was reached from 2.6 to 8.2 GHz with a maximum value of -40 dB at 3 GHz. The improved absorption can be attributed to an optimal electromagnetic match and an enhanced dipole polarization upon increasing of shell thickness. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4747811]
-
Structural and Carbonized Design of 1D FeNi/C Nanofibers with Conductive Network to Optimize Electromagnetic Parameters and Absorption Abilities
Jing Lv,Xiaohui Liang,Guangbin Ji,Bin Quan,Wei Liu,Youwei Du
DOI: https://doi.org/10.1021/acssuschemeng.7b03807
IF: 8.4
2018-01-01
ACS Sustainable Chemistry & Engineering
Abstract:The optimized electromagnetic (EM) parameters are highly indispensable for outstanding microwave absorbers. Generally speaking, it is very necessary to suitably improve permittivity and permeability of the materials. The combination of magnetic/dielectric materials is a good choice. Herein, the irregular shaped FeNi/C composites were synthesized in N-2, atmosphere with unsatisfied EM parameters. To further optimize EM parameters and enhance microwave absorption abilities, constructing one-dimensional (ID) structure is also an excellent scheme. ID FeNi/C nanofibers were successfully obtained by electrospinning technology combined with heat treatment. Enhanced microwave absorption abilities can be fulfilled by conductive network structure, better dielectric loss, and stronger interface polarization intensity. Moreover, carbonized time toward nanofibers plays a key role in microwave absorption, which could influence complex permittivity and dielectric loss of materials. It is found that FeNi/C nanofibers with highly carbonized degree display better microwave absorbing properties. The reflection loss (RL) values less than -10 dB can be observed in 12.8-17.2 GHz (a broad bandwidth of 4.4 GHz) with an absorber thickness of only 1.8 mm. The absorber with a thickness of 2.7 mm has the minimum RL value of -24.8 dB at 9.4 GHz. In this regard, these nanofibers are very likely to be used as EM-wave absorbers in practical application. Furthermore, this work provides a useful strategy to optimize electromagnetic parameters and absorption abilities of metal/carbon absorbers. It may promote the development of 1D metal/carbon composites in microwave absorption field.
-
Preparation and Electromagnetic Absorption Properties of Fe73.2Si16.2B6.6Nb3Cu1 Nanocrystalline Powder
Bingwen Zhou,Mengnan Lv,Jiali Wu,Bin Ya,Linggang Meng,Lanqing Jianglin,Xingguo Zhang
DOI: https://doi.org/10.3390/ma15072558
IF: 3.4
2022-03-31
Materials
Abstract:In order to decrease and control electromagnetic pollution, absorbing materials with better electromagnetic wave absorption properties should be developed. In this paper, a nanocrystalline alloy ribbon with the composition of Fe73.2Si16.2B6.6Nb3Cu1 was designed and prepared. Nanocrystalline alloy powder was obtained by high-energy ball milling treatment. The effects of ball milling time on the soft magnetic properties, microstructure, morphology, and electromagnetic wave absorption properties of alloy powder were investigated. The results showed that, as time increased, α-(Fe, Si) gradually transformed into the amorphous phase, and the maximum saturation magnetization (Ms) reached 135.25 emu/g. The nanocrystalline alloy powder was flakelike, and the minimum average particle size of the powder reached 6.87 μm. The alloy powder obtained by ball milling for 12 h had the best electromagnetic absorption performance, and the minimum reflection loss RLmin at the frequency of 6.52 GHz reached −46.15 dB (matched thickness was 3.5 mm). As time increased, the best matched frequency moved to the high-frequency direction, and the best matched thickness decreased, while the maximum effective absorption bandwidth ΔfRL<−10 dB was 7.22 GHz (10.78–18 GHz).
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
-
Electromagnetic absorption properties of Fe x CoNi magnetic nano particles
Hong Li,Hongyang Li,Feng Yang,Qing Cai,Wenqi Xu,Ran Wang,Ying Liu
DOI: https://doi.org/10.1063/5.0193665
IF: 2.877
2024-04-12
Journal of Applied Physics
Abstract:The microstructure morphology, static magnetic properties, and electromagnetic absorption characteristics of nano FexCoNi alloy particles prepared by chemical liquid deposition with five different Fe content levels are investigated in this paper. The results show that spherical FexCoNi alloy particles with an average particle size of about 100–200 nm and a face-centered cubic crystal structure were obtained. All five samples exhibited soft magnetic behavior, with the saturation magnetization intensity showing an increasing-then-decreasing trend with increasing Fe content, peaking at 141.8 emu/g for Fe content x = 1.0. The dielectric constants (real and imaginary parts) of the prepared alloy particles exhibit significant differences with respect to the variation of Fe content, while the changes in the real and imaginary parts of the magnetic permeability show less pronounced effects with increasing Fe content. As the electromagnetic wave frequency increases, the real parts of the dielectric constants for all composites show minimal fluctuations, and the real parts of the magnetic permeability exhibit a decreasing trend. Moreover, the imaginary parts of the dielectric constants and magnetic permeability show an increasing followed by a decreasing trend as the frequency rises. The material with Fe content x = 1 demonstrated optimal dielectric loss performance and relatively excellent magnetic loss performance, with a sample thickness of 1.9 mm exhibiting the highest reflection loss (RLmax) of −24.2 dB and an effective absorption bandwidth of 4.48 GHz.
physics, applied
-
Microporous Co1−xFex@C nanoparticles: Strong wideband microwave absorbers for reflection loss less than −20 dB
Haoyan Liao,Da Li,Baolei Wang,Qian Wu,Tong Liu
DOI: https://doi.org/10.1016/j.jallcom.2020.158175
IF: 6.2
2021-03-01
Journal of Alloys and Compounds
Abstract:For advanced microwave absorption materials, the bandwidth of reflection loss (RL) ≤ −20 dB is becoming more and more important due to their applications under some extreme occasions where most of the electromagnetic signals must be absorbed. Herein, in-situ carbon-coated Co-Fe-Al precursor nanoparticles (NPs) were prepared by hydrogen plasma metal reaction (HPMR), and then microporous Co1−xFex@C NPs with an average particle size of about 50 nm were successfully prepared by chemical dealloying. They exhibit a distinct core-shell structure with an amorphous carbon shell of approximately 3 nm and a Co1−xFex alloy core containing micropores of 1.1 nm. As the amount of Fe in the microporous Co1−xFex@C NPs increases from 2.1 wt% to 12.0 wt%, the saturation magnetization gradually enlarges from 82.6 to 92.4 emu g−1 whereas the coercive force only decreases slightly. The Co0.98Fe0.02@C sample shows the widest bandwidth (RL ≤ −10 dB) of 11.3 GHz, and surprisingly the bandwidth corresponding to the RL below −20 dB reaches 6.0 GHz, far superior to other Co-based absorbers. Meanwhile, its minimum RL (RLmin) value reaches −102.3 dB with a thickness of 1.8 mm. As the content of Fe increases to 12.0 wt%, the absorption bandwidth (RL ≤ −20 dB) of Co0.88Fe0.12@C sample decreases to 5.7 GHz while its RLmin value strengthens to −133.7 dB. Both the two samples added with Fe exhibit much wider absorption bandwidth (RL ≤ −20 dB) compared with Co@C NPs without Fe addition. The excellent absorption properties are mainly attributed to the facts that microporous morphology promotes the interfacial and dipole polarization, and Fe addition enhances the magnetic resonance. The Co1−xFex@C NPs may pave a new way for designing effective broadband absorbers for RL ≤ −20 dB to meet the high-performance requirements.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
-
Preparation, Electromagnetic and Enhanced Microwave Absorption Properties of Fe Nanoparticles Encapsulated in Carbon Nanotubes
Xiaosi Qi,Jianle Xu,Q. Hu,Wei Zhong,Youwei Du
DOI: https://doi.org/10.1016/j.mseb.2015.04.005
2015-01-01
Abstract:Using hollow Fe2O3 particles as the catalyst, the core/shell structured Fe/carbon nanotube (CNT) hybrid could be synthesized by a chemical vapor deposition method without the hydrogen reduction process. Based on the obtained results, a possible growth mechanism of the Fe/CNT hybrid was discussed. And the investigations of electromagnetic and microwave absorption performances indicate that a minimum reflection loss (RL) value of the obtained sample is ca. -40.15 dB at 17.15 GHz with a matching thickness of 1.5 mm, and the RL value below -20 dB can be obtained in the whole frequency range (1.0-18 GHz) with the sample thickness varies from 1.3 to 10.0 mm. The results demonstrate that a simple and environment-friendly route has been proposed for the production of core/shell structured carbon nanohybrid. The obtained Fe/CNT hybrid exhibits excellent microwave absorption properties and has potential applications in thin thickness and light-weight microwave absorbers. (C) 2015 Elsevier B.V. All rights reserved.
-
Preparation and Microwave Absorption Properties of FeNi Alloy/Carbon Nanotube Composites
Xu Meihua,Zhong Wei,Qi Xiaosi,Du Youwei
DOI: https://doi.org/10.3969/j.issn.1671-4776.2011.04.001
2011-01-01
Abstract:Nanocomposites of FeNi alloy/carbon nanotubes(CNTs)were synthesized by in-situ catalytic decomposition of benzene over FeNi nanoparticles produced by sol-gel fabrication and hydrogen reduction.FESEM and HRTEM investigations reveal that one-dimensional carbon species are produced.The test results of microwave electromagnetism parameters show that the theoretical reflection loss tends to decline at the matching frequency with the increase of the sample thickness.The sample FeNi22@C is an excellent candidate for microwave absorbent when the coating thickness is 1.5 mm,and the reflection loss is-4.74 dB with the frequency of 11.35 GHz.It is probable that by changing the component ratio of FeNi alloy and the absorption thickness of the composites and adjusting the complex permittivity and permeability of the composites,the microwave absorption properties of the composites can be optimized.
-
Construction of FeNi3 and core–shell structured FeNi3@C microspheres toward broadband electromagnetic wave absorbing
Na Chen,Zhang Dong,Xin-Yi Wang,Zhen-Jie Guan,Jian-Tang Jiang,Kang-Jun Wang
DOI: https://doi.org/10.1016/j.apsusc.2022.154337
IF: 6.7
2022-11-30
Applied Surface Science
Abstract:The rational design of electromagnetic wave absorption (EMA) materials featured with broadband and high-efficiency in gigahertz (GHz) is still a great challenge. In this study, we prove fabricating FeNi3 and FeNi3@C core–shell microspheres to solve the challenge. The as-prepared FeNi3 microspheres exhibits extremely broad effective absorption bandwidth (EAB, RL ≥ 10 dB, > 90 % absorbing) of 10.3 GHz (7.7–18.0 GHz) at only 2.0 mm, occupying 64.4 % of the investigated frequency range with a single matching thickness. Such an outstanding EMA performances is credited to strong dielectric loss and magnetic loss. Compared with pristine FeNi3, the delicate design of core–shell structure and tailored synergistic effect of FeNi3 and carbon produce positive reinforcement both in magnetic loss and dielectric loss, endowing FeNi3@C samples with optimized impedance matching and appropriate attenuation ability. As a result, FeNi3@C samples present impressive EMA performances from C to Ku band, especially for FeNi3@C-3, demonstrating its potential of effectively dissipates electromagnetic wave in 6.1–18.0 GHz (RL ≥ 20 dB, > 99 % absorbing) by simply regulating a thickness of 1.5–2.5 mm. FeNi3 and FeNi3@C feature with optional broad bandwidth (completely covering C, X and Ku band), strong absorption, and thin thickness ensure them a superior EMA material.
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
-
Microwave Absorption Properties of Ni-substituted Cobalt Ferrite-Loaded Carbon Nanofiber Composites
Wei Qinqin,Xiao Hongbo,Li Ziming,Zhang Bin,Cai Haopeng
DOI: https://doi.org/10.1007/s10854-021-05451-2
2021-01-01
Journal of Materials Science Materials in Electronics
Abstract:The NixCo1−xFe2O4 (x = 0, 0.25, 0.5, 0.75)/CNFs composites were synthesized in situ by solvothermal method. A series of characterizations of the prepared samples includes X-ray diffraction (XRD), scanning microscope (SEM), vibrating sample magnetometer (VSM) and a vector network analyzer (VNA). XRD and SEM results indicated that the particles have good crystallinity and no other impurities. With the increase of Ni ion doping, the average particle size of the sample gradually decreased, smaller microspheres were beneficial to the bonding of CNFs and Ni0.5Co0.5Fe2O4 particles, and CNFs formed a good encapsulation structure. Combined with the VSM analysis, the change of Ni2+ content results in an increase in the value of Ms, while the values of Mr and Hc decreased slightly, and its magnetic properties were optimized. The complex permittivity and permeability of the NixCo1−xFe2O4/CNFs composites at a frequency of 1–18 GHz were tested by VNA, and the reflection loss (RL) was calculated. The results illustrated that when the Ni2+ doping amount is 50 %, Ni0.5Co0.5Fe2O4/CNFs particles have considerable absorbing performance, the minimum reflection loss reached − 42.24 dB at 14.68 GHz, the effective absorbing frequency band was 4 GHz (12.39–16.40 GHz), and the corresponding matching layer thickness was only 1.5 mm. Therefore, Ni0.5Co0.5Fe2O4/CNFs particles could be used as a thin layer of strong absorbing material.