Abstract:Highlights • Hexagonal Gd 1- x Dy x BO 3 ( x = 0, 0.2, 0.4, 0.6, 0.8, and 1) compounds are synthesized. • They are second-order phase transition materials with ordering temperatures <2 K. • The −ΔSMmax for Gd 1- x Dy x BO 3 ( x = 0.6, 0.8, 1) with Δ H = 2 T surpass 17.3 J/(kg·K). • The −ΔSMmax and RC are enhanced by ∼120% and 70%–110% compared to GdBO 3 , respectively. Borates have attained increasing attention attributed to their excellent thermal stability, distinctive thermodynamic property, and high mechanical strength in recent years. A series of polycrystalline Dy-doped GdBO 3 compounds were prepared, their crystal structures, magnetic properties, and cryogenic magnetocaloric effects were comprehensively investigated. The compounds crystallize in hexagonal structure (space group P 6 3 / mmc ), the lattice constant decreases with the increase of Dy content. Dy-doping in GdBO 3 significantly reduces critical magnetic field and enhances low-field magnetocaloric effect. The maximum magnetic entropy changes for the Gd 1– x Dy x BO 3 ( x = 0.6, 0.8, and 1) compounds in a field change of 2 T surpass 17.3 J/(kg·K) at 2.5 K, enhanced by nearly 120% compared to GdBO 3 (8.0 J/(kg·K)). Besides, the corresponding refrigeration capacity increases from 33.9 J/kg to 62.2, 57.2, and 72.5 J/kg, respectively, with an enhancement of 70%–110%. The considerable maximum magnetic entropy change, refrigerating capacity, and temperature averaged entropy change make them competitive candidates for cryogenic magnetic refrigeration. Graphical abstract A series of hexagonal Gd 1– x Dy x BO 3 compounds undergoes second-order phase transitions below 2 K, being potential cryogenic magnetic refrigerants. The maximum magnetic entropy changes for Gd 1– x Dy x BO 3 ( x = 0.6, 0.8, and 1) with Δ H = 2 T surpass 17.3 J/(kg·K), enhanced by ∼120% compared to GdBO 3 , the refrigeration capacities are enhanced by 70%–110% attributed to the Dy doping. Download : Download high-res image (238KB) Download : Download full-size image

Reversible magnetocaloric effect and refrigeration capacity enhanced by two successive magnetic transitions in DyB2

Comnsb: A Magnetocaloric Material with A Large Low-Field Magnetic Entropy Change at Intermediate Temperature

Large Low-Field Magnetic Entropy Change in Dyco2

Large Magnetocaloric Effect in Antiferromagnetic Ternary Carbide Dy2Cr2C3 Around Liquid Hydrogen Temperature

Large Magnetocaloric Effect and Near-Zero Thermal Hysteresis in the Rare Earth Intermetallic Tb1−x Dy X Co2 Compounds

Enhanced refrigeration capacity in Ho1-Dy B2 compounds around liquid hydrogen temperature

Large Reversible Magnetocaloric Effect in the Ferromagnetic Pyrochlores R2Mn2O7 (R = Dy, Ho, Yb)

Magnetocaloric Properties and Universal Behavior in Electron-Doped Manganite Ca0.88Dy0.12MnO3

Giant Reversible Magnetocaloric Effect in the Pyrochlore Er2Mn2O7 Due to a Cooperative Two-Sublattice Ferromagnetic Order

Excellent Magnetocaloric Performance in the Carbide Compounds RE2Cr2C3 (RE = Er, Ho, and Dy) and Their Composites

Complex Magnetic Properties and Large Magnetocaloric Effects in RCoGe (r=tb, Dy) Compounds

Metamagnetic phase transition induced large magnetocaloric effect in a Dy0.5Ho0.5MnO3 single crystal

Magnetocaloric Effect in Terbium Diboride

Enhanced low-field magnetocaloric effect in Dy-doped hexagonal GdBO 3 compounds

Large Low Field Magnetocaloric Effect in First-Order Phase Transition Compound TlFe3Te3 with Low-Level Hysteresis.

Successive magnetic transitions and magnetocaloric effects in intermetallic compounds RE5Pt3 (RE = Dy, Ho)

Magnetism and giant magnetocaloric effect in rare-earth-based compounds R <sub>3</sub>BWO<sub>9</sub> (R = Gd, Dy, Ho)*

Low-field magnetocaloric effect in (Gd1−xDyx)3Al2 alloys

Large magnetocaloric effect in Gd4Co3

A study of the magnetocaloric behavior of Dy-substituted YMn$_2$O$_5$ compounds

Magnetocaloric effect in the high-temperature antiferromagnet YbCoC2