Abstract:We prepared two kinds of monodispersed polystyrene (PS) microspheres with different surface electrical properties from the polymerization of styrene in water using different initiators. The PS microspheres prepared with potassium persulfate (KPS) as the initiator (PS-a) have negative zeta potential in water, and those prepared with 2,2'-azobis(2-methylpropionamidine) dihydrochloride (AIBA) as the initiator (PS-c) have positive zeta potential in water. Next, PS-a and PS-c microspheres were respectively used as the templates to prepare hollow SiO2 microspheres through a sol-gel process of tetraethoxysilane (TEOS) in an ethanol/ammonia medium. Based on the analysis on the products by FTIR, SEM, TEM, TGA, and N-2 adsorption-desorption isotherms, it was found that the distribution of OH- in the system depended on the surface electrical property of the PS template microspheres, which would lead to different formation processes of the silica shell on the template microspheres. When the PS-a microspheres were used as the template, the OH- ions were repulsed from the negative surface of the PS-a template microspheres, due to the electrostatic repulsion interaction. Thus, the SiO2 nanoparticles with a size of several tens of nanometers were firstly formed by hydrolysis and condensation of TEOS in the medium, and then adsorbed and packed on the surface of PS-a template microspheres through the polar interaction, resulting in the formation of a raspberry-like silica shell with macropores. After the PS-a template microspheres etched by toluene, the raspberry-like hollow silica microspheres were obtained. However, when PS-c template microspheres were used as the template, the OH- ions were adsorbed on the positive surface of the template microspheres. Then, a smooth and dense silica layer was grown directly from the surface of the template microspheres through the hydrolysis and the condensation of TEOS catalyzed by the adsorbed OH- ions. After calcination at 600 degrees C for 8 h, hollow silica microspheres with a smooth and mesoporous silica shell were produced. This work indicates that the morphology of the hollow silica microspheres can be controlled through the surface electrical property of the template microspheres. This study may lead to more applications of hollow silica microspheres in the area of control-release materials, drug carriers, and absorbents.

Preparation of environmental-responsive hollow PNIPAM microspheres using self-removing templates method

Monodisperse Temperature-Responsive Hollow Polymer Microspheres: Synthesis, Characterization and Biological Application

One-Pot Preparation of Hollow Silica Spheres by Using Thermosensitive Poly(N-Isopropylacrylamide) As A Reversible Template

Preparation of Hollow Silica Microspheres Via Poly(N-Isopropylacrylamide)

Preparation of thermoresponsive core–shell polymeric microspheres and hollow PNIPAM microgels

Self-assembly of the Thermosensitive and Ph-Sensitive Pentablock Copolymer PNIPAMx-b-P(tBA-co-AA)90-b-PPO36-b-P(tBA-co-AA)90-b-PNIPAMxin Dilute Aqueous Solutions

Novel Thermo-Responsive Self-Assembly Micelles From A Double Brush-Shaped Pnipam-G-(Pa-B-Peg-B-Pa)-G-Pnipam Block Copolymer With Pnipam Polymers As Side Chains

New Approaches to Stimuli-Responsive Polymeric Micelles and Hollow Spheres

Influence of the Surface Electrical Property of Polymer Template Microspheres on the Morphology of Hollow Silica Microspheres

Preparation of AIE active and thermoresponsive poly(1-ethenyl-4-(1,2,2-triphenylethenyl)-benzene-b-N-isopropylacrylamide) micelles for cell imaging

Preparation of Ph-Sensitive Polyacrylic Acid Hollow Microspheres and Their Release Properties

Synthesis of Hollow Polymer Microspheres with Movable Polyelectrolyte Core and Functional Groups on the Shell-Layer

Preparation and properties of thermo-sensitive organic/inorganic hybrid microgels

Adjustment of responsive temperature and loading behavior of temperature-sensitive core-shell micelles prepared via in-situ polymerization

Preparation and Characterization of Multiresponsive Polymer Composite Microspheres with Core–shell Structure

Preparation and Characterization of Thermosensitive Organic–inorganic Hybrid Microgels with Functional Fe3O4 Nanoparticles As Crosslinker

Effect of crosslinker content on the properties of the micelles prepared via in situ polymerization and preparation of hollow spheres

Thermoresponse improvement of poly(N-isopropylacrylamide) hydrogels via formation of poly(sodium p-styrenesulfonate) nanophases.

One-pot template-free synthesis of monodisperse hollow hydrogel microspheres and their resulting properties.

Preparation and Performance Evaluation of Self-Cementing Nanoscale Polymeric Microspheres with Salt and Temperature Tolerance

Ph-Responsive Hollow Polymeric Microspheres from Irradiated Cyclic Ether Aqueous Solution