Abstract:Eu(BA)3/SiO2 was prepared by means of Eu(BA)3 incorporated into SiO2 matrix using a two step sol-gel method and its luminescent characteristics were investigated. The results show that the optimal parameters of Eu(BA)3/SiO2 prepared are as follows:molar ratio of H2O to TEOS is 4,molar ratio of TEOS to HCl to (CH2)6N4 is 1-7.5×10-4-5×10-3,the precursor solution is converted to wet gel at 40℃ ,molar ratio of HBA to Eu3+ is 3,and Eu(BA)3 doped in material is 1%. Compared with fluorescence spectrum of Eu(BA)3 powder,Eu(BA)3/SiO2 synthesized in above condition has a narrower maximal excitation peak and a small blue shift,from 288 nm to 280 nm in excitation spectra. The 5D0→7F1 and 5D0→7F2 transition emissions of Eu3+ appear at 594 nm and 618 nm in emission spectra,respectively,and the emission intensity of Eu(BA)3/SiO2 is three times as strong as that of Eu(BA)3 powder.

Preparation and luminescent characteristics of compound material Eu(BA)3/SiO2