Structure and luminescence properties of Eu3+ complexes with benzoic acid and 1,10-phenanthroline incorporated in SiO2, SiO2-B2O3 and SiO2-B2O3-Na2O matrices]

Xi-Gui Wang,Hong-Ying Wu,Si-Qin Zhao,Shi-Fu Weng,Jin-Guang Wu

2006-01-01

Spectroscopy and spectral analysis

Abstract:Eu3+ Complexes with benzoic acid and 1, 10-phenanthroline incorporated in SiO2, SiO2-B2O3 and SiO2-B2O3-Na2O matrices were prepared via the sol-gel method. Eu-doped SiO2, SiO2-B2O3 and SiO2-B2O3-Na2O luminescence materials were synthesized. The luminescence of Eu3+ was studied with excitation spectra and emission spectra. Different forms of dopants could influence the luminescence properties. The structure of Eu-doped glass was studied by comparing IR, TEM and XRD. The results showed that after the materials were annealed at 1000 degrees C the structure was very stable because ingredient was already removed totally. The emission spectrum showed that the typical optical spectrum of Eu3+ is D-5(o) -> F-7(i) (j=1, 2) at 588 nm and 614 nm. Comparing EuCl3 with Eu3+ complexes with benzoic acid and 1, 10-phenanthroline as dopant, the latter has strong luminescence property though it has small mass fraction. The luminescence intensity of Eu3+-doped SiO2-B2O3 glass material was weaker than that of Eu3+-doped SiO2 glass material, and the former's spectrum showed that there were Si-O-B bonds. The luminescence intensity of Eu3+ was quenched by this kind of structure. The luminescence intensity of Eu3+-doped SiO2-B2O3-Na2O glass material was greatly increased, and the infrared spectrum illustrated that there was not vibration absorption of Si-O-B bonds. Probably Na replaced B, and Si-O-Na bonds formed. This kind of structure could enhance luminescence intensity of Ea(3+) to some extend.