Abstract:In this paper, we demonstrated the synthesis and electrochemical properties of macro-/ microporous carbon foams (MMCFs) for application as supercapacitor electrode materials. By using Span 80 and Tween 80 as emulsifiers, resorcinol/formaldehyde solution as aqueous phase, and 1iquid paraffin as oil phase, an O/W emulsion was obtained. Macroporous carbon foams were prepared by the polymerization of the emulsion, followed by drying and carbonization. The macroporous carbon foams then were activated at 1273 K by using KOH as an activated agent to obtain MMCFs. The resultant MMCFs were characterized by scanning electron microscopy (SEM) and Brunauer-Emmett-Teller (BET) analyzer. The results indicate that the MMCFs have specific surface areas of 529-670 m2/g, total pore volumes of 0.27-0.33 cm3/g and possess dual pore size distributions with macropore sizes of 0.5-5.0 μm and micropore sizes of 1.72-1.86 nm dependent on the specific experiment parameters. The hierarchical pore structure is propitious to decreases the diffusion resistance of electrolyte and accelerate the ion transfer within the pore channel, and thus improve the electrochemical properties of MMCFs. The electrochemical properties of the MMCFs have been investigated by cyclic voltammetry (CV) and galvanostatic charge-discharge with a three-electrode system in electrolyte of 6 mol/L KOH solution. The CV curves of the MMCFs show quite rectangular curve shape without observation of obvious oxidation-reduction evolution peaks, suggesting a typical nonfaradic adsorption/desorption reaction. The MMCFs present linear galvanostatic charge-discharge curve under the current densities of 1.0-4.0 A/g and their specific capacitance values are 89-110 F/g. The MMCFs has good electrochemical performance and they are good candidates as electrode materials for supercapacitors.

An activated carbon with high capacitance from carbonization of a resorcinol–formaldehyde resin

Preparation and Electrochemical Properties of PF-based Activated Carbon

Water bamboo-derived porous carbons as electrode materials for supercapacitors

Synthesis and Electrochemical Properties of Macro-/Microporous Carbon Foams

Preparation and Electrochemical Characteristics of Electrospun Water-Soluble Resorcinol/Phenol-Formaldehyde Resin-Based Carbon Nanofibers

Resorcinol-formaldehyde based porous carbon as an electrode material for supercapacitors

Preparation and One-Step Activation of Microporous Carbon Nanofibers for Use As Supercapacitor Electrodes

Porous activated carbon derived from petroleum coke as a high-performance anodic electrode material for supercapacitors

Biobased Nano Porous Active Carbon Fibers for High-Performance Supercapacitors

A Novel Synthesis of Hierarchical Porous Carbons from Interpenetrating Polymer Networks for High Performance Supercapacitor Electrodes

Porous Carbon Nanosheets with Abundant Oxygen Functionalities Derived from Phoenix Seeds for High‐Performance Supercapacitor

Hierarchical Activated Mesoporous Phenolic-Resin-based Carbons for Supercapacitors.

Activated Porous Carbon Prepared from Paulownia Flower for High Performance Supercapacitor Electrodes

Nanoporous Carbon Materials Derived from Zanthoxylum Bungeanum Peel and Seed for Electrochemical Supercapacitors

Porous Polyimide-Based Activated Carbon Fibers for CO 2 Capture and Supercapacitor

Nitrogen-Doped Porous Carbons Through Koh Activation with Superior Performance in Supercapacitors

Preparation and electrochemical characterization of an activated carbon material of high specific surface area for supercapacitor

Facile Synthesis of Porous Carbon Derived from Rice Husks with Enhanced Capacitance Performance

Preparation and capacitive performance of PVDC-based activated carbon

Nitrogen, Phosphorus Co-doped Carbon Obtained from Amino Acid Based Resin Xerogel as Efficient Electrode for Supercapacitor

A high-performance carbon derived from polyaniline for supercapacitors