Wood properties of Idesia polycar pa
CHEN Yan,HU Xinyun,CHEN Guoxi,QI Jinqiu,JIANG Yongze,DING Yizhe,XIE Jiulong,HUANG Xingyan,LUO Jianxun
DOI: https://doi.org/10.13207/j.cnki.jnwafu.2023.05.005
2023-01-01
Abstract:【Objective】 The wood properties of Idesia polycarpa were comprehensively investigated by systematical analysis on the anatomical characteristics, physico-mechanical properties and extract composition.【Method】 The 35-year-old I. polycarpa wood in Gulin, Sichuan was selected for material collection and measurement of growth ring width and physico-mechanical properties according to national standards.Anatomical characteristics were analyzed by microtomy and fibre segregation process.The ethyl acetate and anhydrous ethanol extracts were prepared and their constituents were identified using Gas Chromatograph-Mass Spectrometer（GC-MS）.【Result】 I. polycarpa wood was diffuse-porous wood with average ring width of 3.94 mm and the maximum width of 13.0 mm, indicating that I. polycarpa was a high-quality and fast-growing timber species.The average fibre length, width, lumen diameter, double cell wall thickness, aspect ratio and cavity width ratio were 1 420.12 μm, 32.51 μm, 14.40 μm, 5.57 μm and 43.68,respectively.Those values for vessel were 594.34 μm, 89.86 μm, 72.22 μm, 7.58 μm and 6.96,respectively.The average air-dry density of I. polycarpa wood was 0.44 g/cm~3,suggesting that I.polycarpa belonged to soft wood.From air drying to oven drying, the radial, tangential, axial and volume were reduced by 1.61%,3.52% and 0.44%,respectively; while the reduction rates from wet to oven-dry were 3.29%,6.91% and 0.89%,respectively.The average hardness of the end-section, radial-section and tangential-section were 3 377.39,1 814.09 and 1 903.64 N,respectively.The parallel-to-grain compressive strength and bending strength were 35.07 MPa and 64.52 MPa, respectively.The ethanol extract contents for heartwood, transition layer and sapwood were 0.25%,0.75% and 1.15% and the main components were 2,2′-methylenebis-（4-methyl-6-tert-butylphenol）.The ethyl acetate extract contents for heartwood, transition layer and sapwood were 0.56%,1.29% and 0.75% and the main component was 2,4-Di-tert-butylphenol and（3beta, 24S）-stigmast-5-en-3-ol.Small amounts of alcohols and esters were also identified in extracts.【Conclusion】 I. polycarpa wood was yellowish-white to yellowish-brown in color, light and soft in texture and easy to dry, while the compressive strength, bending strength and extract contents were low.I. polycarpa wood was suitable as decoration material, pulping material and artificial boards such as fibreboard, plywood, and particleboard. It was not suitable for compression or curved structures.