Temperature Response and Damage Mechanism of Glass under Thermal Radiation of Strong Explosion
Yixiao Zhang,Qi Zhang
DOI: https://doi.org/10.1016/j.ijheatmasstransfer.2024.125716
IF: 5.2
2024-01-01
International Journal of Heat and Mass Transfer
Abstract:In a strong explosion, the propagation velocity of thermal radiation is much higher than that of the shock wave. The thermal damage caused by thermal radiation and the destruction generated by the shock wave are equally significant for the target, but there is little research on the former. The thermal effect assessment model established in this study simultaneously considers two crucial factors: heat flux and duration, making it more scientific and comprehensive compared to existing models that rely solely on heat flux or heat metering as a single standard to assess thermal effects. When the temperature of 5000 K lasts for 3 s, the surface of single-pane quartz glass has a 0.73 mm softening failure. The quartz glass with a thickness of 10 mm is fully softened when the 5000 K temperature lasts for 107 s. When the fire temperature of 3500 K lasts for 1000s, the softening range of quartz glass is 5.28 mm. The quartz glass with a thickness of 10 mm has a softening range of 0.14 mm when the temperature of 3500 K lasts for 3 s. The softening range increases to 257% (0.36 mm), 400% (0.56 mm), 521% (0.73 mm), and 629% (0.88 mm) when the temperature increases to 4000 K, 4500 K, 5000 K, and 5500 K, respectively. Whether glass can be softened depends on its surface temperature. The critical temperature for quartz glass surface softening is 3269 K, while the complete softening of 10 mm thick quartz glass occurs at 3743 K. The quartz glass with a thickness of 10 mm has a softening range of 0.38 mm when the temperature of 5000 K lasts for 1 s. The softening range increases to 150% (0.57 mm), 192% (0.73 mm), and 226% (0.86 mm) as the duration increases to 2 s, 3 s, and 4 s, respectively. Lead glass is the most prone to suffer softening damage, followed by aluminosilicate glass and quartz glass. The quartz glass has a softening range of 0.73 mm when the temperature of 5000 K lasts for 3 s. The softening range rises to 221% (1.62 mm) for aluminosilicate glass and 319% (2.33 mm) for lead glass, respectively. For aluminosilicate double-pane glass, at 5000 K for 3 s, only the glass pane near the high-temperature source has a softening failure in the range of 1.62 mm. This work reveals the physical process and microscopic mechanism of glass damage under thermal radiation. It provides the scientific basis for glass safety assessment under high temperatures.