Culture of islets on a polyglycolic acid scaffold
Chun Song,Yu-dong Huang,Yan Hou,Yi-min Song,Wan-jun Xie,Ren-ping Huang,Zheng Wei,Zeng-ling Zhang,Yu-bo Shi,Chun-fang Song
DOI: https://doi.org/10.3969/j.issn.1673-8225.2009.16.026
2009-01-01
Abstract:Background: Previous studies have shown that islet cells cultured in vitro for along period can induce hyperplasia of fibrous tissues, cause death of islet, and induce a failure of cell transplantation, so it is important to improve in vitro culture condition for islet cells. Objective: By implanting islets on polyglycolic acid (PGA) scaffolds, to explore growth, morphology, and secretion of islet cells in order to an ideal in vitro survival environment. Design, Time And Setting: An in vitro contrast experiment was performed at the Key Laboratory of Cell Transplantation of the National Ministry of Public Health, the First Affiliated Hospital of Harbin Medical University between June 2005 and December 2008. Materials: PGA scaffold (diameter 15 μ m, mesh 100-150 μ m, porosity 97%, and thickness 1.0-2.0 mm) was used in this study. The PGA scaffold was cultured in 75% alcohol solution for 30 minutes, rinsed with PBS three times, stored in 10 g/L poly-L-lysine for 30 minutes, and sterilized for preparation. Methods: Islets were isolated and digested by Collagenase-V method. Islet in the control group was cultured with RPMI-1640 culture medium containing 20% fetal bovine serum, 2 g/L penicillin-streptomycin-amphotericin, and 10 mmol/L Hepes. While, islet in the scaffold group was implanted on poly-L-lysine-coated PGA scaffold and cultured with the same RPMI-1640 culture medium at the density of 0.6×10 3. Cells in the two groups were incubated in 5% CO 2 incubator at 37 °C. Main Outcome Measures: Number and purity of islet were detected using dithizone staining; survival rate was measured using MTT method; islet content in supernatant was measured using radioimmunity method; adherent growth was observed under scanning electron microscopy. Results: Islets isolated and digested were stained red by dithizone and no stain was observed in the islet exocrine gland. The purity of islets was ≥ 85%. The results of MTT and functional detection showed that the survival rate of islets in the scaffold group was significantly higher than control group (P < 0.05). The observation under scanning electron microscopy demonstrated that islets tightly adhered to the PGA scaffolds and grew in the three-dimensional status. Conclusion: Co-culture of islets and PGA scaffold can improve the survival rates, function and morphology of islets, and prolong the survival time of islets in vitro.