Microstructure and properties of high strength, high conductivity Cu-2.5Fe-0.3Cr-0.3Mg-0.2Si-0.1Ca-0.1Zr alloy treated by multi-stage thermomechanical treatment
Xiaojun Li,Ruixi Tang,Haoran Huang,Xinchen Ma,Wenting Qiu,Liangyu Zheng,Guohui Chao,Yongru Wang,Shen Gong
DOI: https://doi.org/10.1016/j.matchar.2023.113601
IF: 4.537
2023-12-28
Materials Characterization
Abstract:In the Cu-2.5Fe-0.3Cr-0.3 Mg-0.2Si-0.1Ca-0.1Zr alloy, a double-scale (micro and nano) FeCrSi second phase has been generated. The orientation relationship between nano-precipitates and the matrix is: (111)Cu//(202)Fe x Cr (3- x ) Si, 11 ̄0 Cu// 11 ̄1 ̄ Fe x Cr (3- x ) Si. The influence of the thermomechanical treatment process on the microstructure, mechanical properties and electrical conductivity of the alloy is explored. Results indicate that the final alloy has excellent properties. The hardness, yield strength, tensile strength and electrical conductivity of the final alloy are 204 HV, 635 MPa, 649 MPa and 63.57 %IACS, respectively. The calculations show that precipitation strengthening and dislocation strengthening have essential contributions to the strength of the final alloy. The former mainly comes from the strengthening effect of the FeCrSi nano-precipitates, and the latter is related to the multi-stage thermomechanical treatment process.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing