Synthesis And Application Of Several Series Of Polymerizable Surfactants In Emulsion Polymerization
Wei-Hong Qiao,Mo Chen,Hong-Zhu Liu,Xing-Shun Zhao,Cui Cao
2010-01-01
Abstract:After emulsion polymerization, conventional surfactants adsorb in physical action to the surface of latex particles. The adsorption is so weak that the surfactants would desorb from the surface of latex particles in some situations. Polymerizable surfactants, which contain a polymerizable group, can be bound covalently to the surface of latex particles, and then most adverse effects caused by conventional surfactants can be avoided. By using polymerizable surfactants, the stability of the latex and water resistance of the film can be improved.Sodium monoalkyl maleates (named series A), and sodium monoalkylpoly-oxyethylene maleates (named series B), these two kinds of anionic polymerizable surfactants were synthesized, by using normal fatty alcohols, alkyl alcohol polyoxyethylene ether and maleic anhydride. It is found that, because of the introducing of polyoxyethylene group, sodium monoalkylpolyoxyethylene maleates have evidently improved the emulsifying capability, especially at low pH values, and enhanced the stability to electrolytes, storage stability, freeze-thaw stability and water absorption of the films, compared with traditional surfactant SDS. On this basis, N-methyl-N-monododecyl- fumaroyl taurines (named series D) were also synthesized, and are confirmed to be correct by IR, MS or NMR. It is also found that, series D sulfonate polymerizable surfactant with carbon chain length of 10, 12, 14 display excellent emulsifying capacity and good acid tolerance. For studied application system, semicontinuous polymerization of vinyl acetate-butyl acrylate - VeoVa 10 - hexafluorobutyl methacrylate, a mono-disperse latex was obtained with very little coagulum with D3 and D4. The results of the stability tests show that the fumaric surfmer can improve the stability of latex against electrolytes and freezing/thawing. In particular, the surfmer can largely reduce the water adsorption of films and resist the deformation of films when exposed to water. Bonding rate of D3 and D4 gets to 90% and 92% by titration. These indicate that the surfmers D3 and D4 of series D ares very effective when used in the studied emulsion polymerization.Two series of cationic surfmers (E, F) were also synthesized, both of which contained polyoxyethylene or alkyl alcohol as a nonionic and hydrophilic group, and quaternary ammonium as a cationic group.Dodecylpolyoxyethylene maleate diester surfactants (named series E) show the high conversions of monomers (96-99%), the minimal amounts of coagulum, and the polydispersity indexes (PDI) lower than 0.1. The data obtained from the polymerization by using the surfmers, shows that the surfmers (E1, E2 and E3) can be used in emulsion polymerization effectively. Compared with traditional surfactant cetyltrimethylammonium bromide (CTAB), the latex stabilized with the surfmer has a better stability to electrolytes, and can resist five freeze/thaw cycles, and can improve performance on the water resistance of films prepared by El, E2, E3. These results proved that nonionic groups had played a certain role in the space stability of latex.[2-(N, N-diethylamino) ethyl] long-chain ethyl fumarate quaternary ammonium salts (named series F) were prepared with maleic anhydride. Their structures are confirmed to be correct by MS or NMR. The results of bonding rate for series F polymerizable surfactants were all 100%.The Minimal Inhibitory Concentration (MIC) of escherichia coli was determined. Bromide quaternary ammonium polymerization surfactants show better germicidal function than chloride quaternary ammonium polymerization surfactants. Whether bromide quaternary ammonium polymerization surfactants or chloride quaternary ammonium polymerization surfactants, the MIC of 12 carbon chains surfactant is lower than 14 carbon chains surfactant. The experiments showed that, except for F1, the surfrners all exit promising results and the excellent polymerization stability. PDI of particles were lower than 0.1. The latex from F4 and F5 can resist 5 freeze/thaw cycles. At room temperature, their latex can resist more than 3 months. Series F can greatly improve the performance on the water resistance of films.Under the dual role of steric stability (polyoxyethylene nonionic groups) and the charge stability (carbonate, sulfonate, quaternary ammonium cationic groups), the surfmers behaved much better in both the stability of the latex or water sensitivity of the film.