Effects of annealing temperature on microstructure and electromagnetic characteristics of FeSiAl alloy

GAO Feng,LI Pengfei,WANG Qun

DOI: https://doi.org/10.3969/j.issn.1001-2028.2009.05.004

2009-01-01

Abstract:Ball-milled FeSiAl alloy powder was vacuum-annealed at different temperatures and was prepared to soft magnetic alloy composite material (SCM). Using scanning electron microscopy、X-ray diffraction and network analyzer, the effects of annealing temperatures on the phase composition、ordering degree、the average grain size and the complex permeability of SCM within 1 MHz~1.5 GHz were studied for the FeSiAl alloy. With the increase of annealing temperature, the ordering degree of DO3 superlattice structure increases from 0.38 to 0.66、the average grain size increases from 36.93 nm to 71.41 nm、the real and imaginary parts of SCM’s complex permeability at the same frequency decrease gradually.