Preparation and Electrochemical Performance of Hierarchical Porous Carbons

乔松,孙刚伟,张建华,宋文华,乔文明,凌立成

DOI: https://doi.org/10.3969/j.issn.1001-3741.2010.01.004

2010-01-01

Abstract:Hierarchical porous carbons with micro/meso/macropores were prepared by a one-step route with resorcinol and formaldehyde as precursors,in-situ synthesized Mg(OH)2 as a template and KOH as reaction catalyst ,precipitating agent and activation agent. The structures of the hierarchical porous carbons were characterized by scanning electron microscopy,transmission electron microscopy,nitrogen adsorption and X-ray diffraction measurements. The electrochemical behavior of the samples was tested by galvanostatic charge-discharge,cyclic voltammetry and electrochemical impedance spectroscopy using 1 mol/L (C2H5)4NBF4/Propylene carbonate (PC) as electrolyte. The results show that the specific surface area and the pore volume of the carbons increase first and then decrease with an increase of mass ratio of KOH to resorcinol. The highest values,1 300 m2/g and 0.89 cm3/g,were achieved,respectively. Moreover,the resultant carbon exhibits excellent capacitance and power performance when was used as the electrode material for electric double-layer capacitor. The highest specific capacitance up to 116 F/g was obtained at a current density 0.1 A/g and the ratio of retained capacitance of the sample was 78%at a current density 5 A/g.