Effect of Ball-Milling Conditions on the Structure,morphology and Performance of LiMn_2O_4 Prepared from Electrolytic MnO_2

KOU Dan,LIU Xing-quan,ZHANG Zheng,LIU Hong-ji,WANG Chao

DOI: https://doi.org/10.3969/j.issn.1008-0511.2012.06.001

2012-01-01

Abstract:The LiMn2O4 cathode materials were synthesized by using industrial electrolytic MnO2(EMD)as raw material and high temperature solid-phase method.The prepared LiMn2O4 was characterized by XRD,SEM,cyclic voltammetry and electrochemical tests,the effects of different ball size and mass ratio on the grain size and morphology of EMD in pre-milling process were investigated in detail,and the effects on electrochemical performance of prepared LiMn2O4 were also studied.The results demonstrated that the prepared LiMn2O4 samples had moderate grain size,uniform distribution and good spinel morphology which are in accordance with theoretical calculation when MnO2 was pre-milled with small-sized(D=6 mm) balls.Under the conditions of 3.40~4.35 V range and ambient temperatures,the initial specific discharge capacity was as high as 120 mAh/g at 0.5C,and the capacity retention rate was 97% after 20 cycles.