Study on Microstructure and Properties of P265GH Steel Plate for Nuclear Reactor Containment

ZHANG Qing-hui,YANG Yan-ping,HE Jin-shan,LIU Yang,CHEN Leng
DOI: https://doi.org/10.3969/j.issn.1003-4226.2013.03.015
2013-01-01
Abstract:As a nuclear power plant containment steel,hot-rolled P265GH steel should have certain yield strength,good impact toughness and a certain degree of radiation-hardness.Microstructure of hot-rolled steel P265GH is analyzed with an optical microscope,scanning electron microscope and EBSD.Surface microstructure of two samples is lamellar pearlite and ferrite,lateral microstructure of two samples is serious banded structure,average bandwidth of NO.1 sample is 7.78×10-4 mm,anisotropy index is 3.79.With electron back scattering diffraction software processing,the average grain size of NO.1 sample is 15.5 μm,and the average grain size of NO.2 sample is 13.6 μm.Yield strength of transverse direction,45° direction and rolled direction was measured by tensile testing machine,yield strength of three directions of NO.1 sample is less than that of NO.2 sample,yield strength distribution of two samples is 260-310 MPa.Experimental results show that P265GH steel microstructure and texture affect the yield strength,and P265GH steel alloying elements affect its irradiation performance.
What problem does this paper attempt to address?