A Composite Scaffold of PLGA Microspheres/fibrin Gel for Cartilage Tissue Engineering: Fabrication, Physical Properties, and Cell Responsiveness.

Haiguang Zhao,Lie Ma,Changyou Gao,Jiacong Shen

DOI: https://doi.org/10.1002/jbm.b.31174

2008-01-01

Journal of Biomedical Materials Research Part B Applied Biomaterials

Abstract:A composite scaffold of poly(L-lactic-co-glycolic acid) (PLGA) microspheres and fibrin gel was fabricated by blending fibrinogen-immobilized PLGA microspheres with fibrinogen and thrombin solution. The PLGA microspheres with a size of 70 similar to 100 mu m were aminolyzed in a hexanediamine/n-propanol solution to introduce free amino groups on their surface. The fibrinogen immobilization was achieved by glutaraldehyde coupling. When the -NH2 content on the microsphere surface was increased from similar to 2 X 10(-8) mol/mg to similar to 4 X 10(-8) mol/mg, the fibrinogen amount was correspondingly increased from similar to 35 mu g/mg to similar to 70 mu g/mg. Measured by UV-VIS spectroscopy, the clotting time of the composite was less influenced by the microsphere amount, but mainly controlled by the thrombin concentration. When the thrombin concentration was higher than 15 U/mL, the gelation could be finished within 1 min and yielded a composite with evenly suspended and distributed PLGA microspheres. Blending With the microspheres could significantly improve the elastic modulus of the hydrogel as well, whereas less influence on the chondrocyte proliferation and extracellular matrix production. (C) 2008 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 88B: 240-249, 2009