Relationship Of Fragility And Dilatation With Glass-Forming Ability Of Pr-Based Bulk Metallic Glasses
Qingge Meng,Shuguang Zhang,Mingxu Xia,Jianguo Li,Xiufang Bian
2009-01-01
Abstract:Bulk metallic glasses (BMGs) have enabled the measurements of various physical as well as mechanical properties that were often impossible. There have been many studies focusing on the Angell's fragility parameter m [J. Non-Cryst. Solids 131, 13 (1991)] and dilatation of BMGs. However, the fragility parameter m in undercooled melts can not be used to predict the glass-forming ability (GFA) since the fragility parameter m can only be gotten after the glass has been obtained. To predict GFA, in particular, of marginal metallic glasses, a fragility parameter, M, for superheated liquid was empirically proposed by Bian [Phys. Lett. A 335, 61-67(2005)]. On the other hand, thermal expansion is one of the most important thermodynamic characteristics and is strongly correlated to the amorphous structures of metallic glasses. Nonetheless, few research works has paid attention to the relationship between the dilatation characteristics and GFA. Therefore, it is of particular interest to deduce the expression of the parameter M, and to study the correlation of the both fragility parameters, M and M, and dilatation behavior with GFA of BMGs. The results on this topic particularly for Pr-based BMGs will be discussed and summarized in this article.By measuring the viscosity and specific heat capacity of the supercooled liquid, it was found that the Pr55Ni25Al20 alloy behaved much closer to strong glasses than the other reported metallic glasses, and the GFA is correlated more strongly with the liquid/crystal Gibbs free energy difference than with the supercooled melt fragility parameter m. To improve the predictive power for GFA, in particular, of marginal metallic glasses with the parameter M, the refinement to this parameter was made from both the thermodynamic and kinetic perspectives. The refined parameter gives a much better reflection of GFA for metallic glasses. A correlation between alpha(aver) and the weighted average of the thermal expansion coefficients alpha(i) for the constituent elements was found as alpha(aver)=Sigma f(i) alpha(i) for Pr-based BMGs. By assuming Lennard-Jones (U) type potentials, the average nearest-neighbor distances r(1) and the depths of the effective pair potentials V-0 were calculated. The values of r(1) were in good accordance with the experimental results and V-0 correlated with the GFA. The above mentioned results will help to gain deep insight into the glass formation of metallic glasses.