Abstract:In this study, crystalline poly(N-isopropylacrylamide-co-acrylic acid) (PNIPAm-co-AAc) nanoparticle network in organic solvents was obtained by self assembling precursor particles in acetone/epichlorohydrin mixture at room temperature followed by inter-sphere crosslinking at ~98 °C. The crystals thus formed can endure solvent exchanges or large distortions under a temporary compressing force with the reoccurrence of crystalline structures. In acetone, the crystals were stable, independent of temperature, while in water crystals could change their colors upon heating or changing pH values. By passing a focused white light beam through the crystals, different colors were displayed at different observation angles, indicating typical Bragg diffraction. Shear moduli of the gel nanoparticle crystals were measured in the linear stress-yield ranges for the same gel crystals in both acetone and water. Syntheses of particles of different sizes and the relationship between particle size and the color of the gel nanoparticle networks at a constant solid content were also presented. Temperature- and pH- sensitive crystalline PNIPAm-co-AAc hydrogel was prepared using osmosis crosslinking method. Not only the typical Bragg diffraction phenomenon was observed for the hydrogel but also apparent temperature- and pH- sensitive properties were performed. The phase behavior of PNIPAm nanoparticles dispersed in water was also investigated using a thermodynamic perturbation theory combined with lightscattering and spectrometer measurements. It was shown how the volume transition of PNIPAM particles affected the interaction potential and determined a novel phase diagram that had not been observed in conventional colloids. Because both particle size and attractive potential depended on temperature, PNIPAM aqueous dispersion exhibited phase transitions at a fixed particle number density by either increasing or decreasing temperature. The phase transition of PNIPAm-co-AAc colloids was also studied. The results from the comparison between pure PNIPAm and charged PNIPAm colloids showed that the introducing of carboxyl (-COOH) group not only contributed to the synthesis of three-dimensional nanoparticle network but also effectively increased the crystallization temperature and concentration range. The phase transitions at both low and high temperatures were observed from the turbidity change by using UV-Vis spectrometer. Centrifugal vibration method was used to make crystalline PNIPAm-co-AAc dispersion at high concentration (8%). The turbidity test proved the formation of iridescent pattern.

A Facile Method to Assemble Pnipam-Containing Microgel Photonic Crystals

Biomimetic Colloidal Photonic Crystals by Coassembly of Polystyrene Nanoparticles and Graphene Quantum Dots

Polymerization-induced Ultrafast and Massive Growth of Colloidal Photonic Crystals on Hydrogel Surface

Assembly of Nanometer-Sized Hollow Sphere Colloidal Crystals for Applications as Tunable Photonic Materials

Fabrication of Colorful Colloidal Photonic Crystal Fibers Via a Microfluidic Spinning Technique

Magnetically Assembled Photonic Crystal Gels With Wide Thermochromic Range And High Sensitivity

Facile fabrication of crack-free photonic crystals with enhanced color contrast and low angle dependence

The Vertical Deposition Self-Assembly Process and the Formation Mechanism of Poly(styrene-Co-methacrylic Acid) Photonic Crystals on Polyester Fabrics

Synthesis and Characterization of Crystalline Assembly of Poly Nisopropylacry-lamide)-co-acrylic Acid Nanoparticles.

Photonic Crystal Materials with Full Spectrum Structural Color Modulated by Co‐Assembly Strategy

Bright Structural Coloration from Organic Polymeric Photonic Crystals with Robust Heat-Resistance

Fabrication of Patterned Photonic Crystals with Brilliant Structural Colors on Fabric Substrates Using Ink-Jet Printing Technology

Fabrication of effect pigments with full visible photonic crystal colors via the shear-induced assembly of multinary colloidal nanoparticles

Rapid visualized hydrophobic-force-driving self-assembly towards brilliant photonic crystals

Synthesis of Poly(styrene-N-hydroxymethyl Acrylamide) Microspheres and Their Application in Patterned Photonic Crystals

Microfluidic fabrication and thermoreversible response of core/shell photonic crystalline microspheres based on deformable nanogels.

Fabrication of Photonic Crystals with Nigrosine-Doped Poly(Mma-Co-Dvb-Co-Maa) Particles

Rapid Fabrication of SiO2-PHEMA Photonic Crystal Hydrogel Composite Microspheres

Easy Approach to Assembling a Biomimetic Color Film with Tunable Structural Colors.

Free-Standing Photonic Crystal Films with Gradient Structural Colors

Tunable Photonic Microspheres of Comb-Like Supramolecules.