Abstract:The transparent SiO2/silicone resin was prepared with tetraethoxysilane(TEOS) and organosiloxane as main materials by the sol-gel technics,then the silicone/amine hybrid hard film was prepared on polycarbonate(PC) by adding amine resin.The effects of the proportion of amine resin on the properties of the hybrid hard film were discussed.The structure,morphology and transmittance of the hybrid coating were characterized by FTIR,UV,TG,SEM and particle size analyzer etc.The results show that the distribution of the hybrid resin particle size is about 162 nm.The alkali resistance of the hybrid film can be significantly improved by adding a small amount of amine resin.After the hybrid film is dipped in the alkali solution for 24 hours,its light transmittance is still up to 90.7%,and can improve the transparency of PC.When the mass percent of amine resin to silicone resin is 2%,the adhesion strength of the hybrid film to PC sheet is 1 grade,and the pencil hardness is 2H.After the heat-treatment at 120 ℃,the hybrid film is smooth,homogenous and densified.However,the thermal stability of the hybrid film is lower slightly than that of the SiO2/silicone hard film.

Effect of Amine Resin on Property of SiO2/Silicone Hybrid Hard Coatings