Abstract:To investigate the improvement of mechanical properties of high-speed steel by silicon addition,M3∶2 high-speed steel with carbon addition of 0.4 wt.% and silicon addition in the range of 0~3.0 wt.% was sintered at 1230 ℃ using vacuum heat treatment furnace,and then followed by double tempering between 500 ℃ and 600 ℃.Effects of silicon addition on phase characteristics and mechanical properties of tempered M3∶2 high-speed steel were investigated by using X-ray diffraction,scanning electron microscopy,and energy spectrum analysis. Phase analysis results show that silicon distributes mainly in tempered martensite and M6C carbides,but rarely in MC carbides. The content of silicon in tempered martensite of high-speed steel increases with the increasing silicon addition. The addition of silicon exerts a crucial role on the the lattice constant of ferrite in tempered martensite. For the case of 0.7 wt.% silicon addition,the alloy exhibits the maximum lattice constant. Mechanical property test results show that suitable silicon addition can improve the secondary hardening effects of M3∶2 high-speed steel. M3∶2 high-speed steel with 0.7 wt.% silicon addition possesses the excellent combination of high hardness and high bending strength after double tempering at 550 ℃.

Effects of Silicon Addition on Tempering Phase and Mechanical Properties of Sintered M3:2 High-Speed Steel