Abstract:Herein, we report a one-pot approach using polymeric micelles as the recyclable template to prepare hybrid yolk-shell or Janus-like nanoparticles (NPs). The micelles were formed by a block copolymer PEG-b-P4VP (EV) in a methanol/water (1/9, v/v) mixture with PEG as the shell and P4VP as the core. In the mixture of the micelles with AIBN (azobiisobutyronitrile), HAuCl4, NIPAM (N-isopropylacrylamide) and MBA (N, N'-methylenebisacrylamide), hybrid NPs could be obtained by simply heating the mixture at 76 degrees C. At this temperature, AIBN that was largely localized within the hydrophobic P4VP core decomposed into radicals, which reduced HAuCl4 to form Au NPs within the core and initiated the copolymerization of NIPAM and MBA at the core-shell interface to form a poly (NIPAM-co-MBA) network (PNM) to cover the core. The micelle template was conveniently removed from the hybrid NPs by decreasing the pH value of the medium to 3.0. At a low pH, the P4VP block chains were fully protonated; thus, EV becomes highly hydrophilic and soluble in the medium. Moreover, the micelle template dissociated and then gradually diffused into the bulk solution phase as individual EV chains. After the removal of the micelle template, Au@void@PNM yolk-shell NPs were formed. However, when the EV micelles (with the core being slightly noncovalently crosslinked) were used as the template, the same process resulted in the Janus-like NPs; moreover, the micelles were recyclable. After the yolk-shell or Janus NPs were separated by centrifugation, the micelles were recovered in the supernatant and then used again as a template for additional cycles of the yolk-shell or Janus-like NPs preparation and the same results were obtained. Both the yolk-shell and the Janus NPs were easily redispersible in water, and they were confirmed to have both thermal sensitivity and photo sensitivity. We believe that the facile and cost-effective preparation of the yolk-shell NPs (with dual sensitivities) and the Janus NPs (with a relatively high structural regularity) by localizing the chemical reactions within different nanodomains of the micelles should generate considerable interest in the fields of polymer chemistry and soft materials.

Soft Template Synthesis of Yolk/Silica Shell Particles

Quaternized Polystyrene Composite Hollow Particles

Preparation of Core-Shell Inorganic Nano-Particles

Formation of Yolk/SiO2 shell structures using surfactantmixtures as template

Freely Tailorable Yolk‐Shell Encapsulation: Versatile Applications in Ultralow‐k Dielectric, Drug Delivery Systems, and Catalysts

Template synthesis of composite hollow spheres using sulfonated polystyrene hollow spheres

Synthesis of Silica/carbon-Encapsulated Core-Shell Spheres: Templates for Other Unique Core-Shell Structures and Applications in in Situ Loading of Noble-Metal Nanoparticles.

Bulk nanobubbles as soft templates in the fabrication of inorganic core-shell particles

A Facile Strategy for in Situ Core-Template-Functionalizing Siliceous Hollow Nanospheres for Guest Species Entrapment

A one-pot approach using recyclable template to prepare dual-responsive yolk–shell or Janus-like nanoparticles

A Novel and Facile Preparation Method of Hollow Silica Spheres Containing Small SiO2 Cores

Synthesis of Silica Hollow Spheres with Diameter Around 50 Nm by Anionic Surfactant

Synthesis of Porous Hollow Organosilica Particles with Tunable Shell Thickness

Asymmetric Flasklike Hollow Carbonaceous Nanoparticles Fabricated by the Synergistic Interaction Between Soft Template and Biomass.

Construction of Yolk@shell Nanocomposite Particles with Controlled Multisized Pore Structures by Monomicelle Confined Assembly

Yolk/shell Nanoparticles: New Platforms for Nanoreactors, Drug Delivery and Lithium-Ion Batteries.

A facile approach to preparation of silica double-shell hollow particles, and their application in gel composite electrolytes

Yolk‐like Micro/Nanoparticles with Superparamagnetic Iron Oxide Cores and Hierarchical Nickel Silicate Shells

Fabrication of Teardrop-Shaped Silica Particles in Polyelectrolyte Diluted Solution Through in Situ Sol–gel Process

Controllable synthesis of silica hollow spheres by vesicle templating of silicone surfactants

Synthesis of Hollow Spheres with Mesoporous Silica Nanoparticles Shell