Abstract:Inorganic fullerene-like tungsten disulfide particles have been proved to have good anti-friction and anti-wear properties as lubricating materials. As far as we know, however, when it is used as a lubricant additive, its behavior and action mechanism in the friction process are rarely studied. Herein, IF–WS2 particles were synthesized by a Chemical Vapor Deposition (CVD) method. The effect of IF–WS2 particle concentrations in the PAO6 oil on the tribological behaviors was investigated with a four-ball wear machine at both 75 and 100 °C. Additionally, the analyzed morphology and composition of nanomaterials and worn surfaces were analyzed by Scanning electron microscopy (SEM), Transmission Electron Microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). The friction behavior in actual working conditions was studied by a wear testing machine. The experimental results show that compared with the original PAO6 oil, at a dispersion of 0.25 wt% in PAO6 oil, the IF–WS2 particles showed the best performance in terms of coefficient of friction, wear scar diameter and wear mass, which significantly reduced by 27%, 43% and 87%, respectively. At the same time, in the process of friction, it was found that IF–WS2 particles accumulated in the depressions to fill the scratches, and adsorption films and chemical films, including FeS2, WS2 and WO3, were formed on the worn surfaces to avoid the direct contact among the friction pairs more effectively, resulting in the improved anti-wear performances. Additionally, the addition of IF–WS2 particles effectively delayed the rise of lubricating oil temperature. In addition, dispersant span 80 can effectively improve the dispersion and stability of IF–WS2 in PAO6. This work provides us for understanding the effective lubrication mechanism of IF–WS2 particles in more detail and having a new acknowledge of the comprehensive performance of IF–WS2/PAO6 oil.

Synthesis of Inorganic Fullerene-Like Ws2 Nanoparticles and Their Lubricating Performance

Synthesis and Thermal Stability of W/WS2 Inorganic Fullerene-Like Nanoparticles with Core–shell Structure

Synthesis of Fullerene-Like Ws2 Nanoparticles in A Particulately Fluidized Bed: Kinetics and Reaction Phase Diagram

Novel Route to WO<i><sub>x</sub></i>Nanorods and WS<sub>2</sub>Nanotubes from WS<sub>2</sub>Inorganic Fullerenes

Novel route to WOx nanorods and WS2 nanotubes from WS2 inorganic fullerenes.

Advance in Research on Inorganic Fullerene-like Tungsten Disulfide Nanoparticals and Nanotubes

Singular tungsten disulfide core-shell and pure tungsten nanostructures

Decoupling reduction–sulfurization synthesis of inorganic fullerene-like WS2 nanoparticles in a particulately fluidized bed

Thin Films of Fullerene-Like MoS2 Nanoparticles with Ultra-Low Friction and Wear

Design and Evaluation the Anti-Wear Property of Inorganic Fullerene Tungsten Disulfide As Additive in PAO6 Oil

Shock-absorbing and Failure Mechanisms of WS2 and MoS2 Nanoparticles with Fullerene-Like Structures under Shock Wave Pressure.

Synthesis and characterizations of inorganic fullerene-like MoS_2 nanoparticles

Synthesis of Uniform WS 2 Nanoflowers Via a Sodium Silicate-Assisted Hydrothermal Process

Synthesis and Characterization of Flower-Like WS2 Nanospheres Via a Facile Hydrothermal Route

Facile synthesis of WS2@GO nanohybrids for significant improvement in mechanical and tribological performance of EP composites

Wear and Friction of Ni-P Electroless Composite Coating Including Inorganic Fullerene-Ws2 Nanoparticles

Microstructure and Preparation of Nano S-W-S New Solid Lubrication System

Atmospheric Pressure Chemical Vapor Deposition: an Alternative Route to Large-Scale Mos2 and Ws2 Inorganic Fullerene-Like Nanostructures and Nanoflowers

Characterization of Nested Hollow Inorganic Fullerene-Like Tungsten Disulfide Nanoparticles Prepared by Solid-Gas Reaction

Continuous Production Of If-Ws2 Nanoparticles By A Rotary Process

Hydrothermal synthesis of variety low dimensional WS 2 nanostructures