Abstract:The synthesized peptide PT2 (DRTSTWR) has been employed as template for preparation of platinum nanoparticles. Platinum crystallites were obtained by the way Of PtCl4 reacting with PT2 immobilized on the surface of protonated PET-N(CH3)(2) film. The platinum nanoparticles ranging from 1 to 2 nm in size were obtained with the free PT2 and PtCl4 Mixed together in a solution at room temperature and pH 7 for 24 h. Both the crystallites and nanoparticles of platinum were characterized by TEM, XPS and EDX. Based on the data above, it was confirmed that PT2 could be utilized as a template for biomimetic synthesis of platinum nanoparticles in vitro. Subsequently, in order to prepare shape and size controllable nanoparticles of platinum, chitosan and sodium polyacrylate with different concentrations were added into the reaction solution respectively, resulting in the variation of the size and shape of the platinum particles. Especially, platinum particles with size ranging from 12 to 15.5 nm which inclined to array in line were obtained when the molar ratio of chitosan to Pt4+ was 5/1 in the solution. In the presence of sodium polyacrylate whose amount was 5 times of Pt4+, more uniformly spherical platinum particles with size of 6 to 8 nm were synthesized.

Preparation of Pt Nanoparticles Templated by Poly(amidoamine) Dendrimers

Preparation and Characterization of Pd Nanoclusters Templated by Pamam Dendrimers

Templatation and Stabilization of Amino-Terminated Poly(amido-Amine) Dendrimer in Formation of Copper Nanoparticles

Preparation and Stability of Copper Particles Formed Using Amino-Terminated Dendrimer As Template

DNA-templated preparation of palladium nanoparticles and their application

Synthesis and Characterization of Dendrimer-Encapsulated Bimetallic Core-Shell Pdpt Nanoparticles

Preparation Of Monodisperse Platinum Nanocrystal Core-Poly(Amidoamine) (Pamam) Dendrimer Shell Structures As Monolayer Films

Electrodeposition of Pt Nanoclusters on the Surface Modified by Monolayer Poly(amidoamine) Dendrimer Film

Studies on the complexation between generation‐4.5 methyl ester‐terminated poly(amidoamine) dendrimer and Pd2+ ions in methanol

Preparation And Catalysis Of Platinum And Palladium Nanoparticles Capped With Polyaryl Ether Trisacetic Acid Ammonium Chloride Dendrimer

Studies on the complexation between generation-4.5 methyl ester-terminated poly(amidoamine) dendrimer and Pd<sup>2+</sup>ions in methanol

Preparation of Gold Nanoparticles in N, N-dimethylformamide in the Presence of Methyl Ester Terminated Poly(amidoamine) Dendrimers

Preparation And Characterization Of Dendrimer-Templated Ag-Cu Bimetallic Nanoclusters

Synthesis, Characterization, and Application of Pdpt and Pdrh Bimetallic Nanoparticles Encapsulated Within Amine-Terminated Poly(Amidoamine) Dendrimers

Dendrimer Templates for the Formation of Silver Nanoparticles

Exploiting Preparation of Platinum Nanocrystals with Peptide PT2 (DRTSTWR)

Preparation of silver nanoparticles using dendrimer as template

Study on the complexes between PAMAM dendrimer and Cd2+ and the preparation of CdS/PAMAM dendrimer nanocomposite

Studies of Preparation of Palladium Nanoparticles Protected by Dendrons

Preparation of Platinum Core–polyaryl Ether Aminediacetic Acid Dendrimer Shell Nanocomposite for Catalytic Hydrogenation of Phenyl Aldehydes

Preparation Of Au Nanoparticles In The Presence Of Low Generational Poly(Amidoamine) Dendrimer With Surface Hydroxyl Groups