Study on growth and properties of Tm3+/Ho3+ doped Gd3Ga5O12 ~2.0 μm infrared laser crystal
Yan, Wang,Chaoyang Tu,Han Zhou,Jianfu Li,Zhenyu You,Zhaojie Zhu
2011-01-01
Abstract:High quality Tm3+:GGG,Yb3+/ Tm3+:GGG,Cr3+/ Tm3+:GGG,Tm3+/Ho3+:GGG and Cr3+/Tm3+/Ho3+:GGG crystals with the largest size φ25 mm×(30-40) mm have been grown by Czochralski method. The absorption spectra, fluorescence spectra as well as fluorescence decay curves of all these crystals were measured at room temperature. The spectral properties were discussed, and Judd-Ofelt theory was used on some crystals to obtain intensity parameters and other important spectral parameters. The emission cross-sections, quantum efficiency of the transitions corresponding to ~2.0 μm wavelength were calculated. The results show that the codopant Yb3+ and Cr3+ made the absorption of Tm:GGG crystal in the bands with peaks near 980 nm and near 451 nm, 628 nm much stronger, which are suitable for pump by LD and Xenon lamp effectively. In the Tm3+ activated crystals, e.g. Tm3+:GGG,Yb3+/Tm3+:GGG, Cr3+/Tm3+:GGG crystals, the strongest emission locates at ~2.0 μm; while in the Ho3+ activated crystals, e.g. Tm3+/Ho3+:GGG,Cr3+/ Tm3+/Ho3+:GGG crystals, the strongest emission locates at ~2.08 μm. Laser characteristics of Cr3+/Tm3+/Ho3+: Gd3Ga5O12 crystal with size φ5 mm×45 mm were measured using the Xenon flash-lamp as the pumping source and 170 mW laser output was achieved within the range of 2.086-2.102 μm.