Third-order optical nonlinearity in Ge-Se-Te chalcogenide glasses
Zhen Yang,Haonan Hu,Qiuli Li,Zheng Zhang,Lei Niu,Jian Wu,Tengxiu Wei,Yuanhuan Sun,Yiming Fang,Xunsi Wang,Zhiyong Yang,Jinfeng Zhou,Rongping Wang
DOI: https://doi.org/10.1016/j.optmat.2021.111208
IF: 3.754
2021-07-01
Optical Materials
Abstract:<p>We have prepared Ge<sub>x</sub>Se<sub>10</sub>Te<sub>90-x</sub> glasses with a composition of x from 17.5 to 26.25 and measured their properties using various diagnosis tools. It was found that, all the glasses have a transmittance more than 40% at a wavelength range from 2 to 15 μm, and linear refractive index <em>n</em><sub>0</sub> decreases but optical bandgap energy E<sub>g</sub> increases with decreasing Te contents in the glasses. We also analysed the evolution of <em>n</em><sub>2</sub> and <em>β</em> as a function of Ge content, both the evolution of <em>n</em><sub>2</sub> and <em>β</em> are close to the prediction by Sheik-Bahae et al. for optical nonlinearity of semiconductors. In all cases, the nonlinear optical refractive index <em>n</em><sub>2</sub> measured at 3.0 μm is larger than that at 2.5 μm due to the two-photon resonance effect, and a maximum nonlinear index is 2.46 × 10<sup>−13</sup> cm<sup>2</sup>/W at composition of Ge<sub>17.5</sub>Se<sub>10</sub>Te<sub>72.5</sub>. Such larger nonlinearity around 10<sup>−13</sup> cm<sup>2</sup>/W observed in the present paper is one order of the magnitude larger than that in S- and Se-based chalcogenide glasses, demonstrating potentials of Te-based glasses for the applications as mid- and far-infrared nonlinear optical devices.</p>
materials science, multidisciplinary,optics