Abstract:Coal tar pitch was ground into powder and hydroformed with high pressure. After pre-oxidation, the pitch was activated by CO2 at high temperature. The effects of different preparation conditions on the yield, pore structure and phenol adsorption capacity of activated carbon were investigated, and activated carbon prepared under suitable conditions had good adsorption performance. A pore volume of 1-10 nm is the main absorption structure according to the analysis of pore size distribution and phenol adsorption capacity. The activated carbon showed high mechanical strength through compressive strength tests. Graphite nanocrystals around 5 nm were observed in the TEM images, and it illustrates that grain refinement results in the high strength. These nanocrystal stacked structures are easier to make and enlarge pores by activation than graphite layer stacked structures. Surface functional groups are considered not to be the active sites of phenol adsorption as suggested by the results of FTIR and Boehm's titration, and acidic oxygen-containing functional groups are harmful to phenol adsorption, which happen to be removed in the reductive preparation atmosphere. The donor-acceptor complex mechanism can be ruled out, and the pi-pi interactions are considered the most likely mechanism. The Langmuir and Reach-Peterson models are better fitted to the adsorption isotherms. Adsorption kinetics fit the intraparticle diffusion model best. Comparison of different activated carbons shows that suitable pore size is important for phenol adsorption. Thermodynamic parameters demonstrate that the adsorption process is spontaneous and exothermic, and the entropy increases. Pitch-based high-strength columnar activated carbon is an effective and low cost adsorbent for phenol wastewater treatment. This carbon nanocrystal material also provides a new direction for catalyst carriers.

Effect of Preoxidation with HNO3 and Air on Preparation of Pitch-Based Spherical Activated Carbon

Effect of Nitric Acid Pretreatment on the Properties of Activated Carbon and Supported Palladium Catalysts

Preparation of Pitch-based Activated Carbon Fibers and Their Catalytic Oxidation Performance for NO

Catalytic Oxidation of NO at Room Temperature by Pitch-Based Activated Carbon Fibers

Preparation and characterization of pitch coke from oxidized polymerized pitch

Effect of Nitrogen Doping on the Reduction of Nitric Oxide with Activated Carbon in the Presence of Oxygen

Effect of the air oxidation stabilization of pitch on the microstructure and sodium storage of hard carbons

Preparation of pitch-based carbon materials by pyrolysis and their electrocatalytic activity in oxygen reduction reaction

Nitrogen Doping of Activated Carbon Loading Fe2O3 and Activity in Carbon-Nitric Oxide Reaction

Evaluating of the oxidative behaviors of isotropic pitch fractions for optimal the mechanical properties of isotropic pitch-based carbon fibers

Investigation on promotion effect of oxidative stabilization for pitch‐based fiber by co‐carbonization of coal tar pitch and atmospheric residual

Effects of the degree of oxidation of pitch fibers on their stabilization and carbonization behaviors

Effect of Activated Carbon and Its Surface Property on the Activity of Ru/Ac Catalyst

Surface Oxidation of Activated Electrospun Carbon Nanofibers and Their Adsorption Performance for Benzene, Butanone and Ethanol

Research on Coal Tar Pitch Catalytic Oxidation and Its Effect on the Emission of PAHs during Co-Carbonation with Coal

A study on the preparation of pitch-based high-strength columnar activated carbon and mechanism of phenol adsorption from aqueous solution

The Effects of Preparing Conditions on the Performance of Sulfonated Carbon-based Solid Acid

Effect of pre-oxidation process on V2O5/AC catalyst for the selective catalytic reduction of NOx with NH3

Catalytically oxidation of NO into NO2 at room temperature by graphitized porous nanofibers

Improvement of Activated Carbon from Jixi Bituminous Coal by Air Preoxidation