Abstract:In the present study, bismuth sulfide (Bi2S3) nanoribbons were prepared by the hydrothermal method using bismuth nitrate (Bi(NO3)3 x 5H2O), thioacetamide (C2H5NS) and nitrilotriacetic acid (C6H9NO6) as raw materials at 180 degrees C for 12 h. The reaction time was largely reduced and the route has been unreported. The constituent, structure and morphology of the products were characterized by XRD, XPS and TEM, respectively. The powder X-ray diffraction (XRD) pattern shows that the Bi2S3 crystals belong to the orthorhombic phase (JCPDS:17-320) with calculated lattice constants a = 1.1106 nm, b = 1.0993 nm and c = 0.3892 nm, which are consistent with the reported values (a = 1.1149 nm, b = 1.1304 nm and c = 0.3981 nm). Transmission electron microscopic (TEM) studies reveal that the appearance of as-prepared Bi2S3 is nanoribbon-like with the typical width of about 100 nm; and the high-resolution transmission electron microscope (HRTEM) image shows that the crystal grows along the y axis. The quantification of X-ray photoelectron spectra (XPS) analysis peaks gives an atomic ratio of 2 : 3 for Bi : S, which is consistent with the given formula of Bi2S3. Furthermore, the Raman and UV-Vis spectra of the product were also studied. Compared with bulk Bi2S3 (236 cm(-1)), the Raman absorption band of the Bi2S3 nanoribbons (195 cm(-1)) red-shifts 41 cm(-1), which is because of the surface effect of nanomaterials. Furthermore, the product has absorption at the wavelength of about 450 nm in the UV-Vis region. The direct bang gap energy (Eg) was estimated to be about 1.58 eV(Eg of the bulk Bi2S3 is 1.3 eV), which indicates that the product has potential application in the optical and electrical areas.

Preparation Of Uniform Bi2s3 Nanorods Using Xanthate Complexes Of Bismuth(Iii)

Preparation of Bi2S3 nanorods via a hydrothermal approach

A Single-Source Approach to Bi2s3 and Sb2s3 Nanorods Via A Hydrothermal Treatment

Pii: s0025-5408(01)00734-6

Preparation And Characterization Of Bismuth Sulfide Single Crystal Nanorods In Ionic Liquids

Low-temperature Synthesis and Growth Mechanism of Uniform Nanorods of Bismuth Sulfide

Preparation of Uniform Bi2S3 Nanoribbons at a Low Temperature

Preparation of Bi2S3 nanorods by microwave irradiation

Sonochemical Method for the Preparation of Bismuth Sulfide Nanorods

A rational route to synthesize Bi2S3 nanorods in large scale

Large-Scale Synthesis of Bismuth Sulfide Nanorods by Microwave Irradiation

Solvothermal Growth Of Single-Crystal Bismuth Sulfide Nanorods Using Bismuth Particles As Source Material

Polyol-mediated preparation of Bi2S3 nanorods

Syntheses, Growth Mechanism, and Optical Properties of [001] Growing Bi2S3 Nanorods

Study on Preparation and Properties of Bismuth Sulfide Nanotubes

Facile Solvothermal Synthesis of Single-Crystalline Bi2S3 Nanorods on a Large Scale

Long Bi2s3 Nanowires Prepared by A Simple Hydrothermal Method

Controlled Synthesis of High Crystalline Bismuth Sulfide Nanorods: Using Bismuth Citrate As A Precursor

Study on the Preparation and Spectral Characteristics of Bi2s3 Nanoribbons

Preparation and Formation Mechanism of Cu3SbS3 Nanorods

Low Temperature Growth of Bismuth Sulfide Nanorods by a Hydrothermal Method