Layered Cobalt Phosphonate with Metamagnetism
Cai Zhongsheng,Bao Songsong,Zheng Limin
DOI: https://doi.org/10.6023/a12100839
2013-01-01
Abstract:Two layered cobalt phosphonates, namely, CO2(L)(H2O)(2)center dot 0.3H(2)O (1) and Co-2(L)(H2O) (2) (H4L=C6H5CH2N-(CH2PO3H2)(2)) have been synthesized under hydrothermal condition. Single-crystal X-ray diffraction determinations reveal that compound 1 crystallizes in triclinic space group P-1, with a=6.320(1) angstrom, b=9.484(1) angstrom, c=12.705(1) angstrom, a = 91.7(1)degrees,beta=96.2(1)degrees, gamma=103.9(1)degrees, V=733.8(1) angstrom(3), Z=2 and compound 2 crystallizes in monoclinic space group P2(1)lc, with a=14.165(2) angstrom, b=9.574(1) angstrom, c=10.072(1) angstrom, beta=102.5(1)degrees, V=1333.4(3) angstrom(3), Z=4. Both compounds display layered structures in which the inorganic layers made up of tetranuclear clusters of {Co4O6} and {PO3C} linkages are separated by the methylphenyl groups. However, the tetranuclear clusters are different in the two compounds. In 1, the {Co4O6} cluster is composed of edge-sharing {Co(1)NO5} and {Co(2)O-6} octahedra in a zigzag arrangement. While in 2, the equivalent edge-sharing {Co(1)NO5} octahedra are each corner-shared with the {Co(1)O-5} triangular bipyramids, forming a butterfly-like tetramer. Magnetic measurements are conducted for compound 1 which shows a dominant antiferromagnetic interactions between the Co(II) centers. Moreover, metamagnetism is observed for 1 at low temperature with a critical field of 26.0 kOe at 2 K. The dehydrated sample, 1-de, was also prepared by heating 1 at 180 degrees C for 20 min. Magnetic measurement reveals that 1-de exhibits field-induced spin-flop transition with H-sF of 28.0 kOe at 1.8 K. CCDC: 908112 (1), 908113 (2).