Abstract:Bamboo–wood composites have found extensive applications in the container flooring, furniture, and construction industries. However, commonly utilized bamboo units such as four-side-planed rectangular bamboo strips and bamboo scrimber suffer from either low utilization rates or high adhesive content. The recently developed bamboo-flattening technology, which employs softening methods with saturated high-pressure steam, may improve the utilization rate and reduce the adhesive content, but its complex processes and high cost restrict its widespread application. This study introduces a novel bamboo–wood composite utilizing high-utilization, easy-to-manufacture bamboo units processed through a straightforward flattening-and-grooving method. However, the stress concentration introduced by the grooving treatment may affect the mechanical properties and stability of the bamboo–wood composites. In order to optimize the mechanical properties and bonding performance, response surface methodology based on a central composite rotatable design was used to map the effects of hot-pressing parameters (time, temperature, and pressure) on the mechanical properties. The bamboo-woodbamboo–wood composites prepared with optimized conditions of 1.18 min/mm pressing time, 1.47 MPa pressure, and a 150 °C temperature had a 121.51 MPa modulus of rupture and an 11.85 GPa modulus of elasticity, which exhibited an error of only ~5% between the experimental and model predictions. Finite element analysis revealed that, in comparison to homogeneous flat bamboo composites, grooved bamboo composites exhibited distinct tensile ductility and toughness due to discontinuous stress fields and alternating rigid–soft layers, which alter the stress transmission and energy dissipation mechanisms. Additionally, grooving treatment not only effectively improved the surface wettability of the bamboo plants, thus enhancing the permeability of the adhesive, but also facilitated adhesive penetration into parenchymal cells and fibers. This led to the formation of a more robust glue–nail structure and chemical bonding.

Bonding Strength and Damage Modes of Bamboo-Poplar Epoxy Laminates

Interlaminar Shear Strength of Bamboo-Poplar Epoxy Laminates

Mechanical Properties of Aged Glue Laminated Bamboo for Structural Members

Experimental study on mechanical behavior of glue laminated bamboo Ⅰ-joists

Mechanical Behavior of Glued Laminated Bamboo Moment-Resisting Connections

Design Embedment Strength Of Plybamboo Panels Used For Glubam

The Off-Axis Embedment Performance of Bamboo Panels Used for Glubam Structures

A Novel Bamboo–Wood Composite Utilizing High-Utilization, Easy-to-Manufacture Bamboo Units: Optimization of Mechanical Properties and Bonding Performance

Interlaminar Fracture Behaviour of Re-Formed Bamboo/aluminium Sheet Laminates

Influence of Resin Content and Density on Water Resistance of Bamboo Scrimber Composite from a Bonding Interface Structure Perspective

Bond quality of poplar plywood reinforced with hemp fibers and lignin-phenolic adhesives

Evaluation of the dowel-bearing properties and failure modes of engineering-use laminated flattened-bamboo composite by experimental study and micro-analysis

Epoxy‐POSS toughened phenol‐formaldehyde resin adhesive and its enhancement on the interfacial bonding strength of bamboo based composite

Wetting mechanism and interfacial bonding performance of bamboo fiber reinforced epoxy resin composites

Experimental study and analysis of the bond-anchorage properties of laminated flattened-bamboo lumber connections with glued-in steel rod

Physical and dynamic mechanical properties of continuous bamboo reinforcement/bio-based epoxy composites

Effect of crack size, thickness and span on the transverse mode I fracture characteristics of laminated flattened-bamboo lumber

Structural performance of laminated-bamboo lumber nailed connection

Mechanical Response and Failure Mechanisms of Natural Bamboo Fiber Reinforced Poly-Benzoxazine Composite Subjected to Split-Hopkinson Tensile Bar Loading

Effect of heat treatment on bonding performance of poplar via an insight into dynamic wettability and surface strength transition from outer to inner layers

Effects of Cross-Section Morphology, Vascular Bundle Content and Anisotropy on Compression Failure of Laminated Bamboo Columns