Abstract:Abstract Due to the high conductivity and stability of silver, silver ink has been widely used in the field of printed electronics. However, since mechanical strain would cause the contact between key particles to be broken. Recently, higher requirements have been put on the bending resistance of silver paste. In this experiment, by preparing Ag NPs: Ag Flakes composite materials of 20:80 and 30:70 respectively, a new method for preparing stable modified flake silver powder is proposed, and the attachment and growth methods of Ag NPs reduced on micron flake silver powder is discussed. Flake silver powder, dispersant and reducing agent are added to the silver-ammonia complex, and the nano-silver particles are reduced on the flake silver powder by controlling the reaction conditions. When Ag + : Ag Flakes in the solution is 30:70, there is a clear interface between the silver particles and the silver flakes, and the size distribution range is between 10 and 100 nm; when Ag + : Ag Flakes is 20:80, the distance between the nano-silver particles and the silver plate crystal plane is about 0.222 nm and 0.260 nm, these spacings represent the (1–12) and (004) planes of Ag, respectively. The reduced silver particles grow on the surface of the silver sheet, the size is about 5 ∼ 60 nm, and form a sheet-point combination of shaped silver powder, which can be used to make conductive silver paste with cost and performance competitiveness. The reaction can be completed at room temperature (5 ∼ 25 °C) and atmospheric pressure (80 ∼ 100 kPa), the operation is simple, the reaction time is short, and it has a positive effect on the commercial production of printable highly conductive silver paste.

Synthesis of Silver Nanoparticles with Flake-Like Shapes

Rapid Synthesis of High-Stable Silver Nanoparticles by Electrochemical Method

Morphology and Composition Controlled Synthesis of Flower-Like Silver Nanostructures.

Preparation and Characterization of Size Controllable Spherical Silver Nanoparticles

Synthesis of Silver and Gold Nanoparticles by a Novel Electrochemical Method

Synthesis and formation mechanism of micron-size silver flakes with high radius-thickness ratio: application to silver paste

A Facile And Green Synthesis Of Stable Silver Nanoparticles

Silver nanocrystals with special shapes: controlled synthesis and their surface-enhanced Raman scattering properties

Shape-Controlled Synthesis of Gold and Silver Nanoparticles

Controllable synthesis and Ostwald ripening of silver nanoparticles

Study on the Preparation of Spherical Nanosilver Particles Using Ammonium Citrate and Polyvinyl Alcohol as Surfactants

Synthesis of Silver Nanoparticles by Electrochemical Method

Preparation of Disperse Silver Particles by Chemical Reduction

Synthesis of hexagonal flake silver powder

Seed-mediated Synthesis of Silver Nanoplates:Effects of Aging Process on Production

Size-Controlled Synthesis of Highly Water-Soluble Silver Nanocrystals

Surfactant-Directed Synthesis of Silver Nanorods and Characteristic Spectral Changes Occurred by Their Morphology Evolution

PVP-assisted sonoelectrochemical growth of silver nanostructures with various shapes

Study on the mechanism of forming silver nanoparticles on micron-scale flake silver powder

A Facile Green Synthesis of Silver Nanoparticles Based on Poly-L-Lysine

Shape Controllable Synthesis of Silver Nanostructures by a Facile Tannic Acid Reducing Approach