Bismuth-Based Halide Double Perovskite Cs 2 LiBiCl 6 : Crystal Structure, Luminescence, and Stability
Yanming Sun,Alberto José Fernández-Carrión,Yunhui Liu,Congling Yin,Xing Ming,Bo-Mei Liu,Jing Wang,Hui Fu,Xiaojun Kuang,Xianran Xing,Alberto José Fernández-Carrión
DOI: https://doi.org/10.1021/acs.chemmater.1c00854
IF: 10.508
2021-07-26
Chemistry of Materials
Abstract:A new bismuth-based halide double perovskite Cs2LiBiCl6 was isolated successfully using solid-state reactions. The crystal structure was investigated using X-ray diffraction and complemented by 7Li solid-state nuclear magnetic resonance spectroscopy, which indicated the highly ordered nature of Li and Bi ions in the B sublattice of double perovskite. Compared with the Na analogue, the more moisture-sensitive Cs2LiBiCl6 has a smaller indirect band gap of 3.15(2) eV and red-shift luminescence of around 612 nm as well as stronger intensities at Mn2+ doping. The stability mechanism of Cs2LiBiCl6 was discussed together with that of Cs2NaBiCl6 and their inaccessible Br counterparts based on the tolerance and octahedral factors and density functional theory (DFT) calculations. Owing to the small size of Li+ cations, Cs2LiBiCl6 has low tolerance and octahedral factors close to the boundary between the stable perovskite and nonperovskite compounds, which possess a small decomposition energy and thus easily coexist with other ternary phases. The Br-based compositions of Cs2LiBiBr6 and Cs2NaBiBr6 have even smaller octahedral factors and negative decomposition energies, and therefore their double perovskite polymorphs are destabilized. DFT simulations indicate that the moisture sensitivity of Cs2LiBiCl6 is related to the coordination preference of Li+ due to its smaller size and the steric effect from water molecules, in contrast with the larger Na+ showing a more stable octahedral configuration under the water incorporation. These mechanisms combining the geometry factors and decomposition energies provide new insights into the stability of halide double perovskites.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.chemmater.1c00854.XRD patterns of the Cs2LiBiCl6 products with chemical composition tuning; XRD patterns of the Cs2B′BiX6 (B′ = Li+ and Na+, X = Cl– and Br–) sample from the solution-based methods and solid-state reactions; In situ variable temperature XRD patterns of Cs2LiBiCl6; SEM image, EDS elemental mapping, and 7Li SSNMR spectrum of the Cs1.92Li1.08BiCl6 and the Cs2Li1–xBi1–xMn2xCl6 (x = 0.024) sample; charge densities of Cs2LiBiCl6 and Cs2NaBiCl6; XRD patterns of the Cs2Li1–xBi1–xMn2xCl6 sample; Rietveld XRD plot for Cs2Li0.95Bi0.95Mn0.10Cl6; magnetic susceptibilities for the x = 0.024 composition; CIE diagram for the Mn2+-doped Cs2LiBiCl6 and its Na analogue; excitation spectra versus UV–visible absorption spectra for the x = 0.004 composition; calculated decomposition energies (ΔHd) of Cs2B′BiX6 (B′ = Li and Na, X = Cl and Br); refined structural parameters for Cs2LiBiCl6 with disordered Bi and Cs sites; Mn contents determined by the ICP measurement (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical