Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

A Simple and Practical Method for the Preparation of Magnetite Nanowires

Morphology-controlled Synthesis and Characterization of MnWO4 Nanocrystals Via a Facile, Additive-Free Hydrothermal Process

Hydrothermal Preparation and Characterization of MnWO4Nanowires

Selective Synthesis of Fe 2 O 3 and Fe 3 O 4 Nanowires Via a Single Precursor: A General Method for Metal Oxide Nanowires

Synthesis and Magnetic Properties of Single-Crystalline Magnetite Nanowires

One-step wet chemistry for preparation of magnetite nanorods

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

A new simple hydrothermal preparation of nanocrystalline magnetite Fe3O4

Facile and rapid synthesis of nickel nanowires and their magnetic properties

Preparation of Water-Soluble Magnetite Nanocrystals Through Hydrothermal Approach

Fabrication of Mn2O3 Nanowire with Ultra Fine Morphology Via an Electrospinning Technology

Long Bi2s3 Nanowires Prepared by A Simple Hydrothermal Method

Preparation of Three-Dimensional Nano-Magnetite/chitosan Rod

Growth and Nanoscale Magnetic Properties of Ferromagnetic Nanowire Encapsulated Inside Carbon Nanotubes

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Hydrothermal Preparation of Long Nanowires of Vanadium Oxide

Preparation of CNTs-supported Fe3O4 and Fe3C Nano-particles and the Investigation on their Magnetic Properties

Synthesis of necklace-like magnetic nanorings.

Large-scale Fabrication of Single-Crystalline Mn3O4 Nanowires Via Vapor Phase Growth

Preparation and magnetic properties of CoFe2O4 nanowires