Abstract:Eight quaternary rare-earth chalcogenides, RbNd{sub 2}CuS{sub 4}, RbSm{sub 2}CuS{sub 4}, CsLa{sub 2}CuSe{sub 4}, CsSm{sub 2}CuSe{sub 4}, RbEr{sub 2}Cu{sub 3}S{sub 5}, CsGd{sub 2}Ag{sub 3}Se{sub 5}, CsTb{sub 2}Ag{sub 3}Se{sub 5}, and Rb{sub 2}Gd{sub 4}Cu{sub 4}S{sub 9}, have been synthesized at 973 K with the use of a reactive flux of A{sub 2}Q{sub 3} (A=Rb, Cs; Q=S, Se). All structural data were obtained at 153 K. The isostructural compounds ALn{sub 2}CuQ{sub 4} (Ln=rare earth) crystallize with four formula units in the KGd{sub 2}CuS{sub 4} structure type in space group Cmcm of the orthorhombic system; the isostructural compounds Aln{sub 2}M{sub 3}Q{sub 5} (M=Cu, Ag) crystallize with four formula units in the RbSm{sub 2}Ag{sub 3}Se{sub 5} structure type in space group Cmcm of the orthorhombic system; and Rb{sub 2}Gd{sub 4}Cu{sub 4}S{sub 9} crystallizes with two formula units in space group C2/m of the monoclinic system. The cell dimensions of ALn{sub 2}CuQ{sub 4} (a, b, c ({angstrom})) are as follows: RbNd{sub 2}CuS{sub 4}, 4.0762(3), 13.954(1), 13.964(1); RbSm{sub 2}CuS{sub 4}, 4.0391(3), 13.815(1), 13.860(1); CsLa{sub 2}CuSe{sub 4}, 4.3129(6), 14.959(2), 14.798(2); CsSm{sub 2}CuSe{sub 4}, 4.2066(3), 14.6101(9), 14.5164(9). The corresponding R{sub 1} indices for the refined structures are 0.0264, 0.0196, 0.0258, and 0.0224. The cell dimensions of ALn{sub 2}M{sub 3}Q{submore » 5} are as follows: RbEr{sub 2}Cu{sub 3}S{sub 5}, 3.9283(3), 13.897(1), 16.348(1); CsGd{sub 2}Ag{sub 3}Se{sub 5}, 4.2943(4), 15.424(1), 17.501(2); CsTb{sub 2}Ag{sub 3}Se{sub 5}, 4.2779(4), 15.429(2), 17.426(2). The R{sub 1} indices are 0.0257, 0.0255, and 0.0241. The cell dimensions of Rb{sub 2}Gd{sub 4}Cu{sub 4}S{sub 9} (a, b, c ({angstrom}), ({sup o})) is 13.897(1), 3.9883(3), 16.054(1), 109.273(1), and the R{sub 1} index is 0.0199. All eight compounds have closely related three-dimensional tunnel structures. All alkali metal atoms in the tunnels are coordinated to eight Q atoms. Their anionic frameworks are built from LnQ{sub 6} octahedra and MQ{sub 4} tetrahedra. ALn{sub 2}CuQ{sub 4} contains {sup 1}{sub {infinity}}[CuQ{sub 3}] chains of vertex-sharing tetrahedra; Rb{sub 2}Gd{sub 4}Cu{sub 4}S{sub 9}contains {sup 1}{sub {infinity}}[Cu{sub 4}S{sub 8}] chains of tetrahedra; and ALn{sub 2}M{sub 3}Q{sub 5} contains {sup 2}{sub {infinity}}[M{sub 3}Q{sub 5}] layers of tetrahedra. Rb{sub 2}Gd{sub 4}Cu{sub 4}S{sub 9} and RbEr{sub 2}Cu{sub 3}S{sub 5}, which are paramagnetic, obey the Curie-Weiss law, and have effective magnetic moments of 7.9( 2) {mu}{sub B} for Gd{sup 3+} and 9.43(5) {mu}{sub B} for Er{sup 3+}. A band gap of 1.94 eV for Rb{sub 2}Gd{sub 4}Cu{sub 4}S{sub 9} was deduced from its diffuse reflectance spectrum, and the typical 4f-4f optical transitions for Er{sup 3+} were found in RbEr{sub 2}Cu{sub 3}S{sub 5} at about 1.6, 1.9, and 2.5 eV.« less

Rbcu1.2ag3.8se3 And Cscu2sb2se5: Novel Quaternary Intermetallics Synthesized From Superheated Organic Medial

ChemInform Abstract: Novel Sandwiched Intermetallic Selenoantimonates: Soft Synthesis and Characterization of Cu2SbSe3×0.5en and Cu2SbSe3×en.

Insight into the Controllable Synthesis of Cu(I)/Cu(II) Metal–Organic Complexes: Size-Exclusive Selective Dye Adsorption and Semiconductor Properties

Effect of Noncovalent Interactions on Ag(i)/Cu(ii) Supramolecular Architecture for Dual-Functional Luminescence and Semiconductive Properties

New Layered Materials: Syntheses, Structures, and Optical and Magnetic Properties of CsGdZnSe3, CsZrCuSe3, CsUCuSe3, and BaGdCuSe3.

New Quaternary Selenoantimonates AHgSbSe3 (A = Rb, Cs): Synthesis, Structures and Optical Properties

Syntheses and Structures of the New Quaternary Rubidium Selenides RbLn2CuSe4 (ln=sm, Gd, Dy), Rb1.5Ln2Cu2.5Se5 (ln=gd, Dy), and RbSm2Ag3Se5

Syntheses, Structures, and Physical Properties of the New Quaternary Rare-Earth Chalcogenides RbNd2CuS4, RbSm2CuS4, CsLa2CuSe4, CsSm2CuSe4, RbEr2Cu3S5, CsGd2Ag3Se5, CsTb2Ag3Se5, and Rb2Gd4Cu4S9

Sr4Cu25.37(18)Sb12 and Eu4Cu26.06(13)Sb12: Copper-Rich Antimonide Intermetallics with Cage Structure

K2MM‘3Se6(M = Cu, Ag; M‘ = Ga, In), A New Series of Metal Chalcogenides with Chain−Sublayer−Chain Slabs: ∞1[M‘se4]−∞2[(mse4)(m‘se4)]−∞1[m‘se4]

CRYSTAL STRUCTURE OF THE QUATERNARY SEMICONDUCTOR COMPOUND CuFeCrSe3

Syntheses, Structures, and Physical Properties of the New Quaternary Rare-Earth Chalcogenides RbNd

Synthesis, Crystal and Electronic Structures, and Physical Properties of Caged Ternary Cu-Rich Antimonide: BaCu7.31(3)Sb5

Rb 2 CuSb 7 S 12 : Quaternary Antimony-Rich Semiconductor Featuring a Three-Dimensional Open Framework and Exhibiting an Intriguing Photocurrent Response

Hydrazine-hydrothermal Syntheses, Characterizations and Photoelectrochemical Properties of Two Quaternary Chalcogenidoantimonates(iii) BaCuSbQ3 (Q = S, Se)

Crystal Structures And Semiconductor Properties Of Alkline Metal Selenides Mhgsbse3(M = K, Rb, Cs)

Rb2CuSb7S12: Quaternary Antimony-Rich Semiconductor Featuring a Three-Dimensional Open Framework and Exhibiting an Intriguing Photocurrent Response.

K(2)MM'(3)Se(6) (M = Cu, Ag; M' = Ga, In), A new series of metal chalcogenides with chain-sublayer-chain slabs: (infinity)(1)[M'Se(4)]-(infinity)(2)[(MSe(4))(M'Se(4))]-(infinity)(1)[M'Se(4)].

[Mn(en)3]cdsnte4 and [mn(en)3]ag6sn2te8: New Intermetallic Tellurides Synthesized in Superheated Organic Medium

Structural Diversity And Electronic Properties Of Cu2snx3 (X = S, Se): A First-Principles Investigation

Syntheses, crystal structure, and photoelectric properties of two selenoantimonates A–Zn–Sb–Se (A = Rb and Cs)