Abstract:With the goal of improving processability of imide oligomers and achieving of high temperature carbon fiber composite, a series of Thermosetting Matrix Resin solutions (TMR) were prepared by polycondensation of aromatic diamine (3,4′-oxybisbenzenamine, 3,4-ODA) and diester of biphenylene diacid (BPDE) using monoester of 4-phenylethynylphthalic acid (PEPE) as end-capping agent in ethyl alcohol as solvent to afford phenylethynyl-endcapped poly(amic ester) resins with calculated molecular weight (Calc’d Mw) of 1500–10,000. Meanwhile, a series of reactive diluent solutions (RDm) with Calc’d Mw of 600–2100 were also prepared derived from aromatic diamine (4,4′-oxybisbenzenamine, 4,4-ODA), diester of asymmetrical biphenylene diacid (α-BPDE) and monoester of 4-phenylethynylphthalic acid (PEPE) in ethyl alcohol. Then, the TMR solution was mixed with the RDm solution at different weight ratios to afford a series of A-staged thermosetting blend resin (TMR/RDm) solutions for carbon fiber composites. Experimental results demonstrated that the thermosetting blend resins exhibited improved melt processability and excellent thermal stability. After being thermally treated at 200 °C/1 h, the B-staged TMR/RDm showed very low melt viscosities and wider processing window. The minimum melt viscosities of ≤50 Pa·s was measured at ≤368 °C and the temperature scale at melt viscosities of ≤100 Pa·s were detected at 310–390 °C, respectively. The thermally cured neat resins at 380 °C/2 h showed a great combination of mechanical and thermal properties, including tensile strength of 84.0 MPa, elongation at breakage of 4.1%, and glass transition temperature (Tg) of 423 °C, successively. The carbon fiber reinforced polyimide composite processed by autoclave technique exhibited excellent mechanical properties both at room temperature and 370 °C. This study paved the way for the development of high-temperature resistant carbon fiber resin composites for use in complicated aeronautical structures.

Progress in RTM Polyimide Matrix Resins and Composites

Review of Matrix Solidification and Forming Processes of Composite Materials

Progress of the Study of Molecular Composites

Synthesis and Properties of PMR-Type Polyimide Composites with Improved Flexibility

Preparation and Characterization of Matrix-Graded Polyimide Composite along Thickness Direction

Recent Research and Development of Matrix Resins for High Temperature Polymer Composites

Resistance-mechanical Effect of Polymer-Matrix Conducting Composites

Advance in High Temperature Polyimide Resin Matrix Composites for Aeroengine

Study on Toughening of Matrix Resins for Advanced Composite

Improved Melt Processabilities of Thermosetting Polyimide Matrix Resins for High Temperature Carbon Fiber Composite Applications

Molding process and properties of polyimide-fiber-fabric-reinforced polyether ether ketone composites

Synthesis and Properties of PMR Matrix Resins of Poly(Pyrrolone-Benzimidazole)s

Resin transfer moulded silica fibre/phenolics composites fabricated via solution impregnation route

Synthesis and Characterization of High Temperature Transfer Molding Polyimide Resins

Progress in Aromatic Polyimide Films for Electronic Applications: Preparation, Structure and Properties

Application and Development of Advanced Polymer Matrix Composites

Research Progress of Phenolic Resin Matrix Composite

Study of Numerous Resins Used in Polymer Matrix Composite Materials

Continuous Fiber Reinforced Thermoplastic Composite Pultrusion with in Situ Polymerizable Methyl Methacrylate: A Review

Synthesis and Studies of Polyimide

Progress in Research on in Situ Synthesis Particulate Reinforced Titanium Matrix Composites