Microstructure and High Temperature Oxidation Resistance of Si-Y<SUB>2</SUB>O<SUB>3</SUB> Co-deposition Coatings Prepared on Nb-silicide-based Ultrahigh Temperature Alloy by Pack Cementation Process: Microstructure and High Temperature Oxidation Resistance of Si-Y<SUB>2</SUB>O<SUB>3</SUB> Co-deposition Coatings Prepared on Nb-silicide-based Ultrahigh Temperature Alloy by Pack Cementation Process
q i tao,Xi-Ping GUO
DOI: https://doi.org/10.3724/SP.J.1077.2009.01219
IF: 1.292
2009-01-01
Journal of Inorganic Materials
Abstract:Si-Y2O3 co-deposition coatings on Nb-silicide-based ultrahigh temperature alloy were prepared by pack cementation processes. The co-deposition holding temperatures were 1050 degrees C, 1150 degrees C and 1250 degrees C, and the holding tunes were 5, 10, 15 and 20h, respectively. The microstructure and isothermal oxidation resistance of the coatings were studied. The results show, that all Si-Y2O3 co-deposition coatings are composed of a (Nb, X)Si-2 (X represents Ti, Hf and Cr elements) outer layer and a (Nb, X)(5)Si-3 transitional layer. Some thin discontinuous (Cr, Al)(2) (Nb, Ti) laves phase precipitates exist between the substrale and (Nb, X)(5)Si-3 transitional layer. EDS analyses reveal that the distribution of Y on the coatings is not uniform. The content of Y in (Nb, X)Si-2 and (Nb, X)(5)Si-3 phases is about 0.46at%-0.57at% while that in (Cr, Al)(2)(Nb,Ti) is about 0.94at%. After oxidation at 1250 degrees C for 5, 10, 20, 50 and 100h respectively, the retained Si-Y2O3, co-deposition coatings still possess double layers structure with their original constituent phases and combine tightly with both scale and substrate. The dense scale developed on Si-T2O3 co-deposition coating during oxidation at 1250 degrees C is composed of TiO2, SiO2, and Cr2O3. Si-Y2O3 co-deposition coatings possess better oxidation resistance than simple Si deposition coatings.