Electrophoretic Deposition of Multi‐Walled Carbon Nanotubes: The Key Role of Plasma Functionalization and Polymerization
Lynn Hein,Sylvain Coulombe,Renzo Cecere,Rosaire Mongrain
DOI: https://doi.org/10.1002/ppap.202400137
IF: 3.877
2024-09-14
Plasma Processes and Polymers
Abstract:The electrophoretic deposition of oxygen‐based plasma functionalized carbon nanotubes was carried out at 5–40 V for 1–60 min. An ethane‐based plasma polymer was added as an interlayer for improved adhesion. Coating thicknesses up to 10 μm were achieved, the elemental composition was 90‐95 at% carbon with the balance element being oxygen, and coating adhesion without damage was confirmed for shear stresses up to 16 Pa. The electrophoretic deposition of multi‐walled carbon nanotubes (MWCNTs) has been well‐researched; however, preparatory steps lead to MWCNT coating contamination and deposits often have weak adhesion to the substrate. This work targets these two weaknesses. First, MWCNTs were functionalized by nonthermal, radiofrequency plasma, producing oxygenated MWCNTs (O‐MWCNTs), with which water‐based suspensions were prepared. Second, an ethane‐based plasma polymer was applied on the metallic substrate as an interlayer to improve coating adhesion. O‐MWCNT coatings were produced at 5–40 V for 1–60 min. Homogeneous coatings with thicknesses up to 10 μm were achieved, the composition was 90‐95 at% carbon with the balance element being oxygen, and coating adhesion without damage was confirmed for shear stresses up to 16 Pa.
physics, condensed matter, applied, fluids & plasmas,polymer science